- 密度 [g/cm3]: 1.43
- 缺口冲击强度: 0.64
- 弯曲模量 [MPa]: 12.96
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.43 g/cc | 0.0517 lb/in³ | ASTM D792 |
| 1.43 g/cc | 0.0517 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.0700 % | 0.0700 % | 50% RH, 24 hrs; ASTM D570 |
| 0.700 % | 0.700 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Time 86400 sec | 0.0010 - 0.0030 in/in @Time 24.0 hour | ASTM D955 |
| 0.0010 - 0.0030 cm/cm @Time 86400 sec | 0.0010 - 0.0030 in/in @Time 24.0 hour | ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0030 - 0.0070 cm/cm @Time 86400 sec | 0.0030 - 0.0070 in/in @Time 24.0 hour | ISO 294 |
| 0.0040 - 0.0070 cm/cm @Time 86400 sec | 0.0040 - 0.0070 in/in @Time 24.0 hour | ASTM D955 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 179 MPa | 26000 psi | ASTM D638 |
| 187 MPa | 27100 psi | ISO 527 | |
| Elongation at Break | 1.6 % | 1.6 % | ISO 527 |
| 1.7 % | 1.7 % | ASTM D638 | |
| Tensile Modulus | 14.7 GPa | 2130 ksi | 1 mm/min; ISO 527 |
| 16.61 GPa | 2409 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 266 MPa | 38600 psi | ASTM D790 |
| 275 MPa | 39900 psi | ISO 178 | |
| Flexural Modulus | 12.96 GPa | 1880 ksi | ASTM D790 |
| 14.7 GPa | 2130 ksi | ISO 178 | |
| Izod Impact, Notched | 0.640 J/cm | 1.20 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.91 J/cm | 9.20 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 34.0 kJ/m² | 16.2 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 8.00 J | 5.90 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Coefficient of Friction, Dynamic | 0.35 | 0.35 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.28 | 0.28 | ASTM D3702 Modified |
| K (wear) Factor | 26.2 x 10-8 mm³/N-M | 13.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 23.6 µm/m-°C @Temperature -40.0 - 40.0 °C | 13.1 µin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 |
| 23.7 µm/m-°C @Temperature -40.0 - 40.0 °C | 13.2 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 | |
| CTE, linear, Transverse to Flow | 41.7 µm/m-°C @Temperature -40.0 - 40.0 °C | 23.2 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 41.7 µm/m-°C @Temperature -40.0 - 40.0 °C | 23.2 µin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 240 °C | >= 464 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| >= 298 °C @Thickness 3.20 mm | >= 568 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| Flammability, UL94 | V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | UL 94 by SABIC-IP |