- 缺口冲击强度: 0.53
- 弯曲模量 [MPa]: 7.92
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.39 g/cc | 1.39 g/cc | ASTM D792 |
| Moisture Absorption | 0.100 % | 0.100 % | 50% RH, 24 hrs; ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 155 MPa | 22500 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 2.5 % | 2.5 % | Type I, 5 mm/min; ASTM D638 |
| Flexural Strength | 195 MPa | 28300 psi | brk, 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 7.92 GPa | 1150 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 0.530 J/cm | 0.993 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.70 J/cm | 5.06 ft-lb/in | ASTM D4812 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1000 - 1.00e+6 ohm-cm | 1000 - 1.00e+6 ohm-cm | ASTM D257 |
| Surface Resistance | 1000 - 1.00e+6 ohm | 1000 - 1.00e+6 ohm | ASTM D257 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 310 °C @Thickness 3.20 mm | 590 °F @Thickness 0.126 in | unannealed; ASTM D648 |