- 密度 [g/cm3]: 1.4
- 缺口冲击强度: 0.74
- 弯曲模量 [MPa]: 20.2
- 热变形温度 [℃]: 240.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | ISO 1183 |
| 1.413 g/cc | 0.05105 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.0700 % | 0.0700 % | 23°C / 50% RH; ISO 62 |
| 0.0800 % | 0.0800 % | 50% RH, 24 hrs; ASTM D570 | |
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm @Time 86400 sec | 0.0010 in/in @Time 24.0 hour | ASTM D955 |
| 0.0012 cm/cm @Time 86400 sec | 0.0012 in/in @Time 24.0 hour | ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0040 cm/cm @Time 86400 sec | 0.0040 in/in @Time 24.0 hour | ASTM D955 |
| 0.0040 cm/cm @Time 86400 sec | 0.0040 in/in @Time 24.0 hour | ISO 294 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 225 MPa | 32600 psi | ASTM D638 |
| 230 MPa | 33400 psi | ISO 527 | |
| Elongation at Break | 1.5 % | 1.5 % | ASTM D638 |
| 1.5 % | 1.5 % | ISO 527 | |
| Tensile Modulus | 24.7 GPa | 3580 ksi | 1 mm/min; ISO 527 |
| 30.75 GPa | 4460 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 325 MPa | 47100 psi | ASTM D790 |
| 346 MPa | 50200 psi | ISO 178 | |
| Flexural Modulus | 20.2 GPa | 2930 ksi | ASTM D790 |
| 24.3 GPa | 3520 ksi | ISO 178 | |
| Izod Impact, Notched | 0.740 J/cm | 1.39 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 6.08 J/cm | 11.4 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 42.0 kJ/m² | 20.0 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 12.0 J | 8.85 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Coefficient of Friction, Dynamic | 0.30 | 0.30 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.32 | 0.32 | ASTM D3702 Modified |
| K (wear) Factor | 111 x 10-8 mm³/N-M | 55.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 12.0 µm/m-°C @Temperature -40.0 - 40.0 °C | 6.67 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 12.1 µm/m-°C @Temperature -40.0 - 40.0 °C | 6.72 µin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 29.3 µm/m-°C @Temperature -40.0 - 40.0 °C | 16.3 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 29.3 µm/m-°C @Temperature -40.0 - 40.0 °C | 16.3 µin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | >= 240 °C | >= 464 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| >= 298 °C @Thickness 3.20 mm | >= 568 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 240 °C | >= 464 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| >= 298 °C @Thickness 3.20 mm | >= 568 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| Flammability, UL94 | V-0 @Thickness 0.770 mm | V-0 @Thickness 0.0303 in | UL 94 by SABIC-IP |