- 熔体流动速率 [g/10min]: 2.4
- 吸水率 [%]: 0.14
- 缺口冲击强度: 0.69
- 拉伸强度 [MPa]: 150.0
- 弯曲模量 [MPa]: 10.5
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.45 g/cc | 1.45 g/cc | ASTM D792 | ||
| Water Absorption | 0.14 % @Time 86400 sec | 0.14 % @Time 24.0 hour | ASTM D570 | ||
| Viscosity | 270000 cP @Shear Rate 1000 1/s, Temperature 400 °C | 270000 cP @Shear Rate 1000 1/s, Temperature 752 °F | Melt; ASTM D3835 | ||
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Thickness 3.18 mm | 0.0010 - 0.0030 in/in @Thickness 0.125 in | 5" x 0.5" x 0.125" bars; ASTM D955 | ||
| Linear Mold Shrinkage, Transverse | 0.015 - 0.017 cm/cm @Thickness 3.18 mm | 0.015 - 0.017 in/in @Thickness 0.125 in | 5" x 0.5" x 0.125" bars; ASTM D955 | ||
| Melt Flow | 2.4 g/10 min @Load 2.16 kg, Temperature 400 °C | 2.4 g/10 min @Load 4.76 lb, Temperature 752 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 80 | 80 | M-Scale; ASTM D785 | ||
| Hardness, Shore D | 86 @Time 1.00 sec | 86 @Time 0.000278 hour | ASTM D2240 | ||
| Tensile Strength | 133 MPa | 19300 psi | ASTM D638 | ||
| Tensile Strength, Yield | 150 MPa | 21800 psi | ISO 527-2/1A/5 | ||
| Elongation at Break | 2.8 % | 2.8 % | 5.0 mm/min; ASTM D638 | ||
| 2.8 % | 2.8 % | ISO 527-2/1A/5 | |||
| Tensile Modulus | 11.0 GPa | 1600 ksi | 5.0 mm/min; ASTM D638 | ||
| 14.4 GPa | 2090 ksi | ISO 527-2/1A/1 | |||
| Flexural Strength | 218 MPa | 31600 psi | ISO 178 | ||
| 221 MPa | 32100 psi | ASTM D790 | |||
| Flexural Modulus | 10.5 GPa | 1520 ksi | ASTM D790 | ||
| 14.9 GPa | 2160 ksi | ISO 178 | |||
| Compressive Strength | 110 MPa | 16000 psi | ASTM D695 | ||
| Shear Strength | 70.3 MPa | 10200 psi | ASTM D732 | ||
| Izod Impact, Notched | 0.690 J/cm | 1.29 ft-lb/in | ASTM D256 | ||
| 5.30 J/cm | 9.93 ft-lb/in | ASTM D4812 | |||
| Izod Impact, Notched (ISO) | 9.00 kJ/m² | 4.28 ft-lb/in² | ISO 180 | ||
| Izod Impact, Unnotched (ISO) | 34.0 kJ/m² | 16.2 ft-lb/in² | ISO 180 | ||
| Coefficient of Friction, Dynamic | 0.080 | 0.080 | Lubricated conditions: 800 fpm and 750 psi; ASTM D3702 | ||
| 0.090 | 0.090 | Lubricated conditions: 75 fpm and 1000 psi; ASTM D3702 | |||
| 0.25 | 0.25 | Dry conditions: 800 fpm and 31.25 psi; ASTM D3702 | |||
| 0.30 | 0.30 | Dry conditions: 200 fpm and 125 psi; ASTM D3702 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 22.0 µm/m-°C @Temperature 0.000 - 150 °C | 12.2 µin/in-°F @Temperature 32.0 - 302 °F | ASTM E831 | ||
| 22.0 µm/m-°C @Temperature -50.0 - 50.0 °C | 12.2 µin/in-°F @Temperature -58.0 - 122 °F | TMA; ASTM E831 | |||
| Specific Heat Capacity | 1.36 J/g-°C @Temperature 50.0 °C | 0.325 BTU/lb-°F @Temperature 122 °F | DSC | ||
| 1.84 J/g-°C @Temperature 200 °C | 0.440 BTU/lb-°F @Temperature 392 °F | DSC | |||
| Thermal Conductivity | 0.400 W/m-K | 2.78 BTU-in/hr-ft²-°F | ASTM E1530 | ||
| Melting Point | 342 °C | 648 °F | Peak; ASTM D3418 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 291 °C | 556 °F | Unannealed; ASTM D648 | ||
| 291 °C | 556 °F | Annealed; ASTM D648 | |||
| Glass Transition Temp, Tg | 152 °C | 306 °F | ASTM D3418 | ||
| Flammability, UL94 | V-0 @Thickness 0.800 mm | V-0 @Thickness 0.0315 in | UL 94 | ||
| V-0 @Thickness 1.60 mm | V-0 @Thickness 0.0630 in | UL 94 | |||
| Processing Properties | Metric | English | Comments | ||
| Rear Barrel Temperature | 366 °C | 691 °F | |||
| Middle Barrel Temperature | 370 °C | 698 °F | |||
| Front Barrel Temperature | 375 °C | 707 °F | |||
| Nozzle Temperature | 380 °C | 716 °F | |||
| Mold Temperature | 175 - 205 °C | 347 - 401 °F | |||
| Drying Temperature | 150 °C | 302 °F | |||
| Dry Time | 4.00 hour | 4.00 hour | |||
| Descriptive Properties | |||||
| Additive | Carbon Fiber + Graphite + PTFE Lubricant | ||||
| Appearance | Black | ||||
| Availability | Africa & Middle East | ||||
| Asia Pacific | |||||
| Europe | |||||
| North America | |||||
| South America | |||||
| Features | Fatigue Resistant | ||||
| Flame Retardant | |||||
| Good Chemical Resistance | |||||
| Good Dimensional Stability | |||||
| Good Wear Resistance | |||||
| High Heat Resistance | |||||
| Forms | Pellets | ||||
| Generic | PEEK | ||||
| Injection Rate | Fast | ||||
| Processing Method | Injection Molding | ||||
| Machining | |||||
| Profile Extrusion | |||||
| Screw Compression Ratio | 2.5:1.0 to 3.5:1.0 | ||||
| Uses | Aircraft Applications | ||||
| Bearings | |||||
| Bushings | |||||
| Film | |||||
| Gears | |||||
| Industrial Applications | |||||
| Profiles | |||||
| Rods | |||||
| Sheet | |||||
| Tubing | |||||