- 熔体流动速率 [g/10min]: 4.0
- 密度 [g/cm3]: 1.3
- 吸水率 [%]: 0.5
- 拉伸强度 [MPa]: 97.0
- 硬度: 126.0
- 脆化温度 [℃]: -65.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in³ | ASTM D792 |
| Water Absorption | 0.50 % | 0.50 % | 24 hrs; ASTM D570 |
| Moisture Absorption at Equilibrium | 0.50 % | 0.50 % | |
| Linear Mold Shrinkage | 0.0070 cm/cm | 0.0070 in/in | |
| Linear Mold Shrinkage, Transverse | 0.012 cm/cm | 0.012 in/in | |
| Melt Flow | 4.0 g/10 min @Load 2.16 kg, Temperature 400 °C | 4.0 g/10 min @Load 4.76 lb, Temperature 752 °F | |
| Spiral Flow | 11.0 cm @Thickness 1.00 mm | 4.33 in @Thickness 0.0394 in | recommended processing conditions |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 99 | 99 | |
| Hardness, Rockwell R | 126 | 126 | |
| Tensile Strength, Yield | 97.0 MPa | 14100 psi | |
| Coefficient of Friction, Dynamic | 0.34 | 0.34 | |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 2.8 @Frequency 1000 Hz | 2.8 @Frequency 1000 Hz | |
| 3.3 @Frequency 1e+6 Hz | 3.3 @Frequency 1e+6 Hz | ||
| Dissipation Factor | 0.0010 @Frequency 1000 Hz | 0.0010 @Frequency 1000 Hz | |
| 0.0040 @Frequency 1e+6 Hz | 0.0040 @Frequency 1e+6 Hz | ||
| Comparative Tracking Index | 150 V | 150 V | |
| Thermal Properties | Metric | English | Comments |
| Specific Heat Capacity | 2.16 J/g-°C | 0.516 BTU/lb-°F | |
| Thermal Conductivity | 0.250 W/m-K | 1.74 BTU-in/hr-ft²-°F | |
| Melting Point | 340 °C | 644 °F | |
| Maximum Service Temperature, Air | 315 °C | 599 °F | |
| Brittleness Temperature | -65.0 °C | -85.0 °F | |
| Glass Transition Temp, Tg | 143 °C | 289 °F | |
| UL RTI, Electrical | 260 °C | 500 °F | |
| UL RTI, Mechanical with Impact | 180 °C | 356 °F | |
| UL RTI, Mechanical without Impact | 240 °C | 464 °F | |
| Flammability, UL94 | V-0 | V-0 | |
| Oxygen Index | 35 % | 35 % | |
| Processing Properties | Metric | English | Comments |
| Drying Temperature | 150 °C | 302 °F | |
| Dry Time | 3 hour | 3 hour | |