- 密度 [g/cm3]: 1.52
- 吸水率 [%]: 0.04
- 缺口冲击强度: 7.5
- 弯曲模量 [MPa]: 11.5
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 1.52 g/cc | 0.0549 lb/in³ | Crystalline; ISO 1183 |
Water Absorption | 0.040 % @Temperature 23.0 °C, Time 86400 sec | 0.040 % @Temperature 73.4 °F, Time 24.0 hour | 3.2mm thick tensile bar; ISO 62-1 |
Water Absorption at Saturation | 0.30 % @Temperature 23.0 °C | 0.30 % @Temperature 73.4 °F | Equilibrium; by immersion; ISO 62-1 |
Viscosity | 290000 cP @Temperature 400 °C | 290000 cP @Temperature 752 °F | melt; ISO 11443 |
Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | 360°C nozzle, 160°C tool; ISO 294-4 |
Linear Mold Shrinkage, Transverse | 0.0090 cm/cm | 0.0090 in/in | 380°C nozzle, 180°C tool; ISO 294-4 |
Spiral Flow | 15.0 cm @Thickness 1.00 mm | 5.91 in @Thickness 0.0394 in | 380°C nozzle, 180°C tool |
Mechanical Properties | Metric | English | Comments |
Hardness, Shore D | 90 @Temperature 23.0 °C | 90 @Temperature 73.4 °F | ISO 868 |
Tensile Strength at Break | 40.0 MPa @Temperature 275 °C | 5800 psi @Temperature 527 °F | ISO 527 |
55.0 MPa @Temperature 225 °C | 7980 psi @Temperature 437 °F | ISO 527 | |
70.0 MPa @Temperature 175 °C | 10200 psi @Temperature 347 °F | ISO 527 | |
115 MPa @Temperature 125 °C | 16700 psi @Temperature 257 °F | ISO 527 | |
190 MPa @Temperature 23.0 °C | 27600 psi @Temperature 73.4 °F | ISO 527 | |
Elongation at Break | 2.4 % @Temperature 23.0 °C | 2.4 % @Temperature 73.4 °F | ISO 527 |
Tensile Modulus | 12.0 GPa @Temperature 23.0 °C | 1740 ksi @Temperature 73.4 °F | ISO 527 |
Flexural Strength | 270 MPa @Temperature 23.0 °C | 39200 psi @Temperature 73.4 °F | ISO 178 |
Flexural Modulus | 11.5 GPa @Temperature 23.0 °C | 1670 ksi @Temperature 73.4 °F | ISO 178 |
Compressive Strength | 55.0 MPa @Temperature 200 °C | 7980 psi @Temperature 392 °F | ISO 604 |
160 MPa @Temperature 120 °C | 23200 psi @Temperature 248 °F | ISO 604 | |
250 MPa @Temperature 23.0 °C | 36300 psi @Temperature 73.4 °F | ISO 604 | |
Izod Impact, Notched (ISO) | 7.50 kJ/m² @Temperature 23.0 °C | 3.57 ft-lb/in² @Temperature 73.4 °F | ISO 180/A |
Izod Impact, Unnotched (ISO) | 50.0 kJ/m² @Temperature 23.0 °C | 23.8 ft-lb/in² @Temperature 73.4 °F | ISO 180/U |
Electrical Properties | Metric | English | Comments |
Volume Resistivity | 5.00e+15 ohm-cm | 5.00e+15 ohm-cm | IEC 60093 |
Dielectric Constant | 3.4 @Frequency 1000 Hz, Temperature 23.0 °C | 3.4 @Frequency 1000 Hz, Temperature 73.4 °F | IEC 60250 |
Dielectric Strength | 19.0 kV/mm @Thickness 2.50 mm | 483 kV/in @Thickness 0.0984 in | IEC 60243-1 |
Dissipation Factor | 0.0040 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 0.0040 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | IEC 60250 |
Thermal Properties | Metric | English | Comments |
CTE, linear | 20.0 µm/m-°C @Temperature <=143 °C | 11.1 µin/in-°F @Temperature <=289 °F | Along flow below Tg; ISO 11359 |
20.0 µm/m-°C @Temperature >=143 °C | 11.1 µin/in-°F @Temperature >=289 °F | Along flow above Tg; ISO 11359 | |
45.0 µm/m-°C @Temperature <=143 °C | 25.0 µin/in-°F @Temperature <=289 °F | Average below Tg; ISO 11359 | |
110 µm/m-°C @Temperature >=143 °C | 61.1 µin/in-°F @Temperature >=289 °F | Average above Tg; ISO 11359 | |
Specific Heat Capacity | 1.70 J/g-°C @Temperature 23.0 °C | 0.406 BTU/lb-°F @Temperature 73.4 °F | DSC |
Thermal Conductivity | 0.300 W/m-K @Temperature 23.0 °C | 2.08 BTU-in/hr-ft²-°F @Temperature 73.4 °F | ISO/CD 22007-4 |
Melting Point | 343 °C | 649 °F | ISO 11357 |
Deflection Temperature at 1.8 MPa (264 psi) | 335 °C | 635 °F | ISO 75-f |
Glass Transition Temp, Tg | 143 °C | 289 °F | Onset; ISO 11357 |
UL RTI, Electrical | 240 °C | 464 °F | UL 746B |
UL RTI, Mechanical with Impact | 240 °C | 464 °F | UL 746B |
UL RTI, Mechanical without Impact | 240 °C | 464 °F | UL 746B |
Flammability, UL94 | V-0 @Thickness 0.500 mm | V-0 @Thickness 0.0197 in | |
Glow Wire Test | 960 °C @Thickness 2.00 mm | 1760 °F @Thickness 0.0787 in | IEC 60695-2-12 |
Processing Properties | Metric | English | Comments |
Mold Temperature | 170 - 200 °C | 338 - 392 °F | |
Drying Temperature | 120 °C @Time 18000 sec | 248 °F @Time 5.00 hour | |
150 °C @Time 10800 sec | 302 °F @Time 3.00 hour |