- 密度 [g/cm3]: 1.32
- 吸水率 [%]: 0.5
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.32 g/cc | 0.0477 lb/in³ | |
| Moisture Absorption at Equilibrium | 0.10 % | 0.10 % | Saturation at 50% RH; ISO 1110; DIN 53714 |
| Water Absorption at Saturation | 0.50 % | 0.50 % | 23°C; ISO 62; DIN 53495 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 97.0 MPa | 14100 psi | ISO 527; DIN 53455 |
| Elongation at Break | 25 % | 25 % | ISO 527; DIN 53455 |
| Tensile Modulus | 3.60 GPa | 522 ksi | ISO 527; DIN 53452 |
| Charpy Impact Unnotched | NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ISO 179; DIN 53453 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | IEC 167; DIN 53482 |
| Dielectric Strength | 20.0 kV/mm | 508 kV/in | IEC 243; DIN 53481 |
| Dissipation Factor | 0.0040 @Frequency 1e+6 Hz | 0.0040 @Frequency 1e+6 Hz | IEC 250; DIN 53483 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 47.0 µm/m-°C @Temperature 20.0 °C | 26.1 µin/in-°F @Temperature 68.0 °F | DIN 53752 |
| Thermal Conductivity | 0.250 W/m-K | 1.74 BTU-in/hr-ft²-°F | DIN 53612 Method A |
| Melting Point | 340 °C | 644 °F | ISO 1218 Method A; DIN 53736 |
| Maximum Service Temperature, Air | 260 °C | 500 °F | 5000 hours; 50% Tensile Strength; IEC 216; DIN 53446 |
| 300 °C | 572 °F | a few hours operation | |
| Deflection Temperature at 1.8 MPa (264 psi) | 152 °C | 306 °F | ISO 75; DIN 53461 |
| Flammability, UL94 | V-0 @Thickness 1.60 mm | V-0 @Thickness 0.0630 in | |