- 密度 [g/cm3]: 1.26
- 吸水率 [%]: 0.4
- 缺口冲击强度: 9.5
- 拉伸强度 [MPa]: 95.0
- 弯曲模量 [MPa]: 4.10
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.26 g/cc | 0.0455 lb/in³ | Amorphous; ISO 1183 | ||
| 1.30 g/cc | 0.0470 lb/in³ | Crystalline; ISO 1183 | |||
| Water Absorption | 0.40 % | 0.40 % | by immersion; ISO 62-1 | ||
| 0.070 % @Time 86400 sec | 0.070 % @Time 24.0 hour | 3.2 mm thick Tensile bar; ISO 62-1 | |||
| Viscosity | 500000 cP @Temperature 400 °C | 500000 cP @Temperature 752 °F | Melt; ISO 11443 | ||
| Linear Mold Shrinkage, Flow | 0.010 cm/cm | 0.010 in/in | 390°C nozzle, 200°C tool; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.013 cm/cm | 0.013 in/in | 390°C nozzle, 200°C tool; ISO 294-4 | ||
| Spiral Flow | 850 cm @Thickness 1.00 mm | 335 in @Thickness 0.0394 in | 390°C nozzle, 200°C tool; Victrex | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 95.0 MPa | 13800 psi | ISO 527 | ||
| Elongation at Break | 45 % | 45 % | ISO 527 | ||
| Tensile Modulus | 3.70 GPa | 537 ksi | ISO 527 | ||
| Flexural Strength | 12.0 MPa @Temperature 275 °C | 1740 psi @Temperature 527 °F | Result based on 450G; ISO 178 | ||
| 17.0 MPa @Temperature 175 °C | 2470 psi @Temperature 347 °F | Result based on 450G; ISO 178 | |||
| 80.0 MPa @Temperature 125 °C | 11600 psi @Temperature 257 °F | Result based on 450G; ISO 178 | |||
| 155 MPa @Temperature 23.0 °C | 22500 psi @Temperature 73.4 °F | ISO 178 | |||
| Flexural Modulus | 4.10 GPa | 595 ksi | ISO 178 | ||
| Compressive Strength | 70.0 MPa @Temperature 120 °C | 10200 psi @Temperature 248 °F | Result based on 450G; ISO 604 | ||
| 120 MPa @Temperature 23.0 °C | 17400 psi @Temperature 73.4 °F | Result based on 450G; ISO 604 | |||
| Izod Impact, Notched (ISO) | 9.50 kJ/m² | 4.52 ft-lb/in² | ISO 180/A | ||
| Izod Impact, Unnotched (ISO) | NB | NB | ISO 180/U | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+9 ohm-cm @Temperature 275 °C | 1.00e+9 ohm-cm @Temperature 527 °F | Result based on 450G | ||
| 1.00e+15 ohm-cm @Temperature 125 °C | 1.00e+15 ohm-cm @Temperature 257 °F | Result based on 450G | |||
| 1.00e+16 ohm-cm @Temperature 23.0 °C | 1.00e+16 ohm-cm @Temperature 73.4 °F | Result based on 450G | |||
| Dielectric Constant | 3.2 @Frequency 50000 Hz, Temperature 23.0 °C | 3.2 @Frequency 50000 Hz, Temperature 73.4 °F | Result based on 450G | ||
| 4.5 @Frequency 50000 Hz, Temperature 200 °C | 4.5 @Frequency 50000 Hz, Temperature 392 °F | Result based on 450G | |||
| Dielectric Strength | 16.0 kV/mm @Thickness 2.50 mm | 406 kV/in @Thickness 0.0984 in | Result based on 450G; IEC 60243-1 | ||
| Dissipation Factor | 0.0030 @Frequency 1.00e+6 Hz | 0.0030 @Frequency 1.00e+6 Hz | Result based on 450G; IEC 60250 | ||
| Comparative Tracking Index | 150 V | 150 V | Result based on 450G; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 35.0 µm/m-°C | 19.4 µin/in-°F | Along flow below Tg, Result based on 450G; ISO 11359 | ||
| 150 µm/m-°C | 83.3 µin/in-°F | Along flow above Tg, Result based on 450G; ISO 11359 | |||
| CTE, linear, Transverse to Flow | 55.0 µm/m-°C | 30.6 µin/in-°F | Average below Tg, Result based on 450G; ISO 11359 | ||
| 140 µm/m-°C | 77.8 µin/in-°F | Average above Tg, Result based on 450G; ISO 11359 | |||
| Specific Heat Capacity | 2.20 J/g-°C | 0.526 BTU/lb-°F | DSC | ||
| Thermal Conductivity | 0.290 W/m-K | 2.01 BTU-in/hr-ft²-°F | ISO/CD 22007-4 | ||
| Melting Point | 343 °C | 649 °F | ISO 11357 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 152 °C | 306 °F | Result based on 450G; ISO 75-f | ||
| Glass Transition Temp, Tg | 143 °C | 289 °F | Onset; ISO 11357 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | <= 100 °C | <= 212 °F | Hopper Temperature | ||
| Nozzle Temperature | 390 °C | 734 °F | |||
| Zone 1 | 370 °C | 698 °F | |||
| Zone 2 | 375 °C | 707 °F | |||
| Zone 3 | 380 °C | 716 °F | |||
| Zone 4 | 385 °C | 725 °F | |||
| Mold Temperature | 190 - 220 °C | 374 - 428 °F | |||
| <= 250 °C | <= 482 °F | ||||
| Dry Time | 3 hour @Temperature 150 °C | 3 hour @Temperature 302 °F | |||
| 5 hour @Temperature 120 °C | 5 hour @Temperature 248 °F | ||||
| Descriptive Properties | |||||
| Color | Natural/Beige | ||||
| Gate | > 1mm or 0.5 x part thickness | ||||
| Runner | Die/nozzle > 3mm, manifold > 3.5mm | ||||