类别：热塑性聚合物；聚合物；ABS；聚碳酸酯/ ABS合金，无筋；聚碳酸酯（PC）
材料说明：主要特点：
•韧性高，即使在较低的温度下
•高尺寸精度和稳定性
•油漆性能良好
•流动性好
等级特征：
•阻燃
•注塑
•薄壁应用
Physical PropertiesMetricEnglishCommentsDensity 1.19 g/cc0.0430 lb/in³ISO 1183-1Moisture Absorption at Equilibrium 0.20 %0.20 %ISO 62, 50% RHWater Absorption at Saturation 0.50 %0.50 %ISO 62Viscosity 240000 cP
@Shear Rate 1000 1/s,
Temperature 260 °C240000 cP
@Shear Rate 1000 1/s,
Temperature 500 °Fmelt viscosity; b.o. ISO 11443-ALinear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm
@Thickness 3.00 mm0.0050 - 0.0070 in/in
@Thickness 0.118 in150x105x3mm; b.o. ISO 2577Linear Mold Shrinkage, Transverse 0.0050 - 0.0070 cm/cm
@Thickness 3.00 mm0.0050 - 0.0070 in/in
@Thickness 0.118 in150x105x3mm; b.o. ISO 2577 Mechanical PropertiesMetricEnglishCommentsTensile Strength at Break 50.0 MPa7250 psi50 mm/min; ISO 527-1,-2Tensile Strength, Yield 65.0 MPa9430 psi50 mm/min; ISO 527-1,-2Elongation at Break >= 50 %>= 50 %50 mm/min; b.o. ISO 527-1,-2Elongation at Yield 4.0 %4.0 %50 mm/min; ISO 527-1,-2Tensile Modulus 2.70 GPa392 ksi1 mm/min; ISO 527-1,-2Izod Impact, Notched (ISO) 30.0 kJ/m²
@Temperature 23.0 °C14.3 ft-lb/in²
@Temperature 73.4 °FISO 180-AIzod Impact, Unnotched (ISO) NB
@Temperature 23.0 °CNB
@Temperature 73.4 °FISO 180-U Electrical PropertiesMetricEnglishCommentsVolume Resistivity 1.00e+17 ohm-cm1.00e+17 ohm-cmIEC 60093Surface Resistance 1.00e+17 ohm1.00e+17 ohmIEC 60093Dielectric Constant 
3.1
@Frequency 1.00e+6 Hz3.1
@Frequency 1.00e+6 HzIEC 60250 3.2
@Frequency 100 Hz3.2
@Frequency 100 HzIEC 60250Dielectric Strength 35.0 kV/mm
@Thickness 1.00 mm889 kV/in
@Thickness 0.0394 inIEC 60243-1Dissipation Factor 0.0050
@Frequency 100 Hz0.0050
@Frequency 100 HzIEC 60250 0.0075
@Frequency 1.00e+6 Hz0.0075
@Frequency 1.00e+6 HzIEC 60250Comparative Tracking Index 325 V325 VSolution A; IEC 60112 Thermal PropertiesMetricEnglishCommentsCTE, linear, Parallel to Flow 76.0 µm/m-°C
@Temperature 23.0 - 55.0 °C42.2 µin/in-°F
@Temperature 73.4 - 131 °FISO 11359-1,-2CTE, linear, Transverse to Flow 80.0 µm/m-°C
@Temperature 23.0 - 55.0 °C44.4 µin/in-°F
@Temperature 73.4 - 131 °FISO 11359-1,-2Deflection Temperature at 0.46 MPa (66 psi) 100 °C212 °FISO 75-1,-2Deflection Temperature at 1.8 MPa (264 psi) 91.0 °C196 °FISO 75-1,-2Vicat Softening Point 106 °C
@Load 5.10 kg223 °F
@Load 11.2 lb50°C/h; ISO 306 108 °C
@Load 5.10 kg226 °F
@Load 11.2 lb120°C/h; ISO 306Flammability, UL94 V-0
@Thickness 0.750 mmV-0
@Thickness 0.0295 in 5VB
@Thickness 1.50 mm5VB
@Thickness 0.0591 inUL 94-5V 5VA
@Thickness 3.00 mm5VA
@Thickness 0.118 inUL 94-5V Processing PropertiesMetricEnglishCommentsMelt Temperature 240 °C464 °FInjection molding; ISO 294Mold Temperature 80.0 °C176 °FInjection molding; ISO 294Injection Velocity 240 mm/sec9.45 in/secISO 294