拜耳 PC/ABS fr3110 共混物

 拜耳 fr3110 PC/ABS 共混物
类别：热塑性聚合物；聚合物；ABS；聚碳酸酯/ ABS合金，无筋；聚碳酸酯（PC）

材料说明：主要特点：

•韧性高，即使在较低的温度下

•高尺寸精度和稳定性

•油漆性能良好

•流动性好

等级特征：

•阻燃

•注塑

•高耐热

•易流动

 Physical PropertiesMetricEnglishCommentsDensity 1.18 g/cc0.0426 lb/in³ISO 1183-1Moisture Absorption at Equilibrium 0.20 %0.20 %ISO 62, 50% RHWater Absorption at Saturation 0.50 %0.50 %ISO 62Viscosity 140000 cP
@Shear Rate 1000 1/s,
Temperature 260 °C140000 cP
@Shear Rate 1000 1/s,
Temperature 500 °Fmelt viscosity; b.o. ISO 11443-ALinear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm
@Thickness 3.00 mm0.0050 - 0.0070 in/in
@Thickness 0.118 in150x105x3mm; b.o. ISO 2577Linear Mold Shrinkage, Transverse 0.0050 - 0.0070 cm/cm
@Thickness 3.00 mm0.0050 - 0.0070 in/in
@Thickness 0.118 in150x105x3mm; b.o. ISO 2577 Mechanical PropertiesMetricEnglishCommentsTensile Strength at Break 50.0 MPa7250 psi50 mm/min; ISO 527-1,-2Tensile Strength, Yield 60.0 MPa8700 psi50 mm/min; ISO 527-1,-2Elongation at Break >= 50 %>= 50 %50 mm/min; b.o. ISO 527-1,-2Elongation at Yield 4.0 %4.0 %50 mm/min; ISO 527-1,-2Tensile Modulus 2.70 GPa392 ksi1 mm/min; ISO 527-1,-2Izod Impact, Notched (ISO) 12.0 kJ/m²
@Temperature 23.0 °C5.71 ft-lb/in²
@Temperature 73.4 °FISO 180-AIzod Impact, Unnotched (ISO) NB
@Temperature 23.0 °CNB
@Temperature 73.4 °FISO 180-U Electrical PropertiesMetricEnglishCommentsVolume Resistivity 1.00e+16 ohm-cm1.00e+16 ohm-cmIEC 60093Surface Resistance 1.00e+16 ohm1.00e+16 ohmIEC 60093Dielectric Constant  3.1
@Frequency 1.00e+6 Hz3.1
@Frequency 1.00e+6 HzIEC 60250 3.2
@Frequency 100 Hz3.2
@Frequency 100 HzIEC 60250Dielectric Strength 30.0 kV/mm
@Thickness 1.00 mm762 kV/in
@Thickness 0.0394 inIEC 60243-1Dissipation Factor  0.0050
@Frequency 100 Hz0.0050
@Frequency 100 HzIEC 60250 0.0070
@Frequency 1.00e+6 Hz0.0070
@Frequency 1.00e+6 HzIEC 60250Comparative Tracking Index 350 V350 VSolution A; IEC 60112 Thermal PropertiesMetricEnglishCommentsCTE, linear, Parallel to Flow 68.0 µm/m-°C
@Temperature 23.0 - 55.0 °C37.8 µin/in-°F
@Temperature 73.4 - 131 °FISO 11359-1,-2CTE, linear, Transverse to Flow 68.0 µm/m-°C
@Temperature 23.0 - 55.0 °C37.8 µin/in-°F
@Temperature 73.4 - 131 °FISO 11359-1,-2Deflection Temperature at 0.46 MPa (66 psi) 101 °C214 °FISO 75-1,-2Deflection Temperature at 1.8 MPa (264 psi) 91.0 °C196 °FISO 75-1,-2Vicat Softening Point  108 °C
@Load 5.10 kg226 °F
@Load 11.2 lb50°C/h; ISO 306 110 °C
@Load 5.10 kg230 °F
@Load 11.2 lb120°C/h; ISO 306Flammability, UL94 V-0
@Thickness 1.50 mmV-0
@Thickness 0.0591 in Processing PropertiesMetricEnglishCommentsMelt Temperature 240 °C464 °FInjection molding; ISO 294Mold Temperature 80.0 °C176 °FInjection molding; ISO 294Injection Velocity 240 mm/sec9.45 in/secISO 294