PTS三星®pc-05gfr 5%概述：
类别：热塑性聚合物；；聚碳酸酯（PC）；聚碳酸酯，玻璃纤维填充，阻燃
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ASTM D792 | ||
| Water Absorption | 0.15 % | 0.15 % | 24 hours at 73°C; ASTM D570 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 120 | 120 | ASTM D785 | ||
| Tensile Strength, Yield | 58.6 MPa @Thickness 3.17 mm |
8500 psi @Thickness 0.125 in |
ASTM D638 | ||
| Elongation at Break | 15 % @Thickness 3.17 mm |
15 % @Thickness 0.125 in |
ASTM D638 | ||
| Flexural Yield Strength | 93.1 MPa @Thickness 3.17 mm |
13500 psi @Thickness 0.125 in |
ASTM D790 | ||
| Flexural Modulus | 2.48 GPa @Thickness 3.17 mm |
360 ksi @Thickness 0.125 in |
ASTM D790 | ||
| Izod Impact, Notched | 1.33 J/cm @Thickness 3.17 mm |
2.49 ft-lb/in @Thickness 0.125 in |
ASTM D256 | ||
| Electrical Properties | Metric | English | Comments | ||
| Arc Resistance | 0.00 - 60 sec | 0.00 - 60 sec | PLC 7 | ||
| Comparative Tracking Index | 175 - 250 V | 175 - 250 V | PLC 3 | ||
| Hot Wire Ignition, HWI | 30 - 60 sec | 30 - 60 sec | PLC 2 | ||
| High Amp Arc Ignition, HAI | >= 120 arcs | >= 120 arcs | PLC 0 | ||
| High Voltage Arc-Tracking Rate, HVTR | 80.0 - 150 mm/min | 3.15 - 5.91 in/min | PLC 3 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 135 °C | 275 °F | ASTM D648 | ||
| UL RTI, Electrical | 125 °C | 257 °F | |||
| UL RTI, Mechanical with Impact | 115 °C | 239 °F | |||
| UL RTI, Mechanical without Impact | 125 °C | 257 °F | |||
| Flammability, UL94 | V-0 @Thickness 3.00 mm |
V-0 @Thickness 0.118 in |
|||
| V-0 @Thickness 6.00 mm |
V-0 @Thickness 0.236 in |
||||
| Processing Properties | Metric | English | Comments | ||
| Rear Barrel Temperature | 221 - 249 °C | 430 - 480 °F | |||
| Middle Barrel Temperature | 266 - 293 °C | 510 - 560 °F | |||
| Front Barrel Temperature | 277 - 299 °C | 530 - 570 °F | |||
| Nozzle Temperature | 249 - 288 °C | 480 - 550 °F | |||
| Melt Temperature | 271 - 299 °C | 520 - 570 °F | |||
| Mold Temperature | 71.1 - 93.3 °C | 160 - 200 °F | |||
| Drying Temperature | 121 °C | 250 °F | |||
| Dry Time | 3 - 4 hour | 3 - 4 hour | 48 hours max. | ||
| Back Pressure | 0.345 - 1.38 MPa | 50.0 - 200 psi | |||
| De |
|||||
| Injection Speed- Edge Gate | Fast | ||||
| Injection Speed- Tab Gate | Fast | ||||
| Injection Speed- Tunnel Gate | Fast | ||||