| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in³ | ISO 1183-1 |
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | ISO 62, 50% RH |
| Water Absorption at Saturation | 0.60 % | 0.60 % | ISO 62 |
| Viscosity | 255000 cP @Shear Rate 1000 1/s, Temperature 260 °C |
255000 cP @Shear Rate 1000 1/s, Temperature 500 °F |
melt viscosity; b.o. ISO 11443-A |
| Linear Mold Shrinkage, Flow | 0.0055 - 0.0075 cm/cm @Thickness 3.00 mm |
0.0055 - 0.0075 in/in @Thickness 0.118 in |
150x105x3mm; b.o. ISO 2577 |
| Linear Mold Shrinkage, Transverse | 0.0055 - 0.0075 cm/cm @Thickness 3.00 mm |
0.0055 - 0.0075 in/in @Thickness 0.118 in |
150x105x3mm; b.o. ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 54.0 MPa | 7830 psi | 50 mm/min; ISO 527-1,-2 |
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | 50 mm/min; ISO 527-1,-2 |
| Elongation at Break | >= 50 % | >= 50 % | 50 mm/min; b.o. ISO 527-1,-2 |
| Elongation at Yield | 4.9 % | 4.9 % | 50 mm/min; ISO 527-1,-2 |
| Tensile Modulus | 2.30 GPa | 334 ksi | 1 mm/min; ISO 527-1,-2 |
| Izod Impact, Notched (ISO) | 40.0 kJ/m² @Temperature -30.0 °C |
19.0 ft-lb/in² @Temperature -22.0 °F |
ISO 180-A |
| 50.0 kJ/m² @Temperature 23.0 °C |
23.8 ft-lb/in² @Temperature 73.4 °F |
ISO 180-A | |
| Izod Impact, Unnotched (ISO) | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 180-U |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
ISO 180-U | |
| Puncture Energy | 46.0 J @Temperature 23.0 °C |
33.9 ft-lb @Temperature 73.4 °F |
ISO 6603-2 |
| 52.0 J @Temperature -30.0 °C |
38.4 ft-lb @Temperature -22.0 °F |
ISO 6603-2 | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+17 ohm-cm | 1.00e+17 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+17 ohm | 1.00e+17 ohm | IEC 60093 |
| Dielectric Constant | 2.9 @Frequency 1.00e+6 Hz |
2.9 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 3.0 @Frequency 100 Hz |
3.0 @Frequency 100 Hz |
IEC 60250 | |
| Dielectric Strength | 35.0 kV/mm @Thickness 1.00 mm |
889 kV/in @Thickness 0.0394 in |
IEC 60243-1 |
| Dissipation Factor | 0.0025 @Frequency 100 Hz |
0.0025 @Frequency 100 Hz |
IEC 60250 |
| 0.0090 @Frequency 1.00e+6 Hz |
0.0090 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 200 V | 200 V | Solution A; IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 75.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
41.7 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1,-2 |
| CTE, linear, Transverse to Flow | 70.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
38.9 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1,-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 128 °C | 262 °F | ISO 75-1,-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 108 °C | 226 °F | ISO 75-1,-2 |
| Vicat Softening Point | 129 °C @Load 5.10 kg |
264 °F @Load 11.2 lb |
50°C/h; ISO 306 |
| 130 °C @Load 5.10 kg |
266 °F @Load 11.2 lb |
120°C/h; ISO 306 | |