热塑性聚合物；聚合物；ABS；聚碳酸酯/ ABS合金，无筋；聚碳酸酯（PC）
材料说明：
中等冲击强度PC / ABS共混物具有高的热变形和加工性能优良。
| 参数： | |||
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | ISO R1183 |
| Water Absorption | 0.20 - 0.60 % | 0.20 - 0.60 % | ISO R 62 |
| Linear Mold Shrinkage | 0.0030 - 0.0070 cm/cm | 0.0030 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 2.5 g/10 min @Load 3.80 kg, Temperature 230 °C |
2.5 g/10 min @Load 8.38 lb, Temperature 446 °F |
ISO 1133 |
| 9.5 g/10 min @Load 5.00 kg, Temperature 250 °C |
9.5 g/10 min @Load 11.0 lb, Temperature 482 °F |
ISO 1133 | |
| 15 g/10 min @Load 5.00 kg, Temperature 260 °C |
15 g/10 min @Load 11.0 lb, Temperature 500 °F |
ISO 1133 | |
| Mechanical Properties | Metric | English | Comments |
| Ball Indentation Hardness | 97.0 MPa | 14100 psi | DIN 53459 |
| Tensile Strength at Break | 46.0 MPa | 6670 psi | ISO R 527 |
| Tensile Strength, Yield | 44.0 MPa | 6380 psi | ISO R 527 |
| Elongation at Break | >= 80 % | >= 80 % | ISO R 527 |
| Tensile Modulus | 2.05 GPa | 297 ksi | ISO R 527 |
| Flexural Strength | 70.0 MPa | 10200 psi | ISO 178 |
| Flexural Modulus | 2.25 GPa | 326 ksi | ISO 178 |
| Izod Impact, Notched | 3.00 J/cm @Temperature -40.0 °C |
5.62 ft-lb/in @Temperature -40.0 °F |
ISO R 180 |
| 5.00 J/cm @Temperature 23.0 °C |
9.37 ft-lb/in @Temperature 73.4 °F |
ISO R 180 | |
| Charpy Impact, Notched | 1.50 J/cm² @Temperature -40.0 °C |
7.14 ft-lb/in² @Temperature -40.0 °F |
ISO R179 |
| 2.00 J/cm² @Temperature 0.000 °C |
9.52 ft-lb/in² @Temperature 32.0 °F |
ISO R179 | |
| 2.50 J/cm² @Temperature 23.0 °C |
11.9 ft-lb/in² @Temperature 73.4 °F |
ISO R179 | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 80.0 - 85.0 µm/m-°C @Temperature 0.000 - 80.0 °C |
44.4 - 47.2 µin/in-°F @Temperature 32.0 - 176 °F |
ASTM D696 |
| Thermal Conductivity | 0.200 W/m-K | 1.39 BTU-in/hr-ft²-°F | ASTM C177 |
| Deflection Temperature at 0.46 MPa (66 psi) | 110 °C | 230 °F | unannealed; ISO 75 B |
| Deflection Temperature at 1.8 MPa (264 psi) | 96.0 °C | 205 °F | unannealed; ISO 75 A |
| Vicat Softening Point | 109 °C | 228 °F | 50°C/hr, 5 kg; ISO 306 B |
| 127 °C | 261 °F | 120°C/hr, 1 kg; ISO 306 A | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| Oxygen Index | 20 % | 20 % | ASTM D2863 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 250 - 280 °C | 482 - 536 °F | |
| Mold Temperature | 60.0 - 90.0 °C | 140 - 194 °F | |