PC/ABS树脂具有机械性能的卓越平衡.低温时也具备的高冲击强度，室内紫外稳定性，高达185°F(85°C)的相对热指数，耐燃性（UL 94 5VB*），色彩范围广泛，易于注塑和挤塑加工。
A35-105 PC/ABS合金的物理性能表解释：
体积电阻率：是材料每单位立方体积的电阻，该试验可以按如下方法进行：将材料在500伏特电压下保持1分钟，并测量所产生的电流，体积电阻率越高，材料用做电绝缘部件的效能就越高。
参数：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.12 g/cc | 0.0405 lb/in³ | ISO R1183 B |
| Water Absorption | 0.20 - 0.60 % | 0.20 - 0.60 % | ISO R 62 |
| Linear Mold Shrinkage | 0.0030 - 0.0070 cm/cm | 0.0030 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 3.0 g/10 min @Load 3.80 kg, Temperature 230 °C |
3.0 g/10 min @Load 8.38 lb, Temperature 446 °F |
ISO 1133 |
| 12 g/10 min @Load 5.00 kg, Temperature 250 °C |
12 g/10 min @Load 11.0 lb, Temperature 482 °F |
ISO 1133 | |
| 17 g/10 min @Load 5.00 kg, Temperature 260 °C |
17 g/10 min @Load 11.0 lb, Temperature 500 °F |
ISO 1133 | |
| Mechanical Properties | Metric | English | Comments |
| Ball Indentation Hardness | 105 MPa | 15200 psi | DIN 53459 |
| Tensile Strength at Break | 50.0 MPa | 7250 psi | ISO R 527 |
| Tensile Strength, Yield | 52.0 MPa | 7540 psi | ISO R 527 |
| Elongation at Break | >= 80 % | >= 80 % | ISO R 527 |
| Tensile Modulus | 2.20 GPa | 319 ksi | ISO R 527 |
| Flexural Strength | 82.0 MPa | 11900 psi | ISO 178 |
| Flexural Modulus | 2.10 GPa | 305 ksi | 3 points; ISO 178 |
| Izod Impact, Notched (ISO) | 50.0 kJ/m² @Temperature -40.0 °C |
23.8 ft-lb/in² @Temperature -40.0 °F |
ISO R 180 |
| 70.0 kJ/m² @Temperature 23.0 °C |
33.3 ft-lb/in² @Temperature 73.4 °F |
ISO R 180 | |
| Charpy Impact, Notched | 2.00 J/cm² @Temperature -40.0 °C |
9.52 ft-lb/in² @Temperature -40.0 °F |
ISO R179 |
| 2.80 J/cm² @Temperature 0.000 °C |
13.3 ft-lb/in² @Temperature 32.0 °F |
ISO R179 | |
| 3.50 J/cm² @Temperature 23.0 °C |
16.7 ft-lb/in² @Temperature 73.4 °F |
ISO R179 | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 75.0 - 80.0 µm/m-°C @Temperature 0.000 - 80.0 °C |
41.7 - 44.4 µin/in-°F @Temperature 32.0 - 176 °F |
ASTM D696 |
| Thermal Conductivity | 0.200 W/m-K | 1.39 BTU-in/hr-ft²-°F | ASTM C177 |
| Deflection Temperature at 0.46 MPa (66 psi) | 126 °C | 259 °F | unannealed; ISO 75 B |
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C | 221 °F | unannealed; ISO 75 A |
| Vicat Softening Point | 122 °C | 252 °F | 50°C/hr, 5 kg; ISO 306 B |
| 142 °C | 288 °F | 120°C/hr, 1 kg; ISO 306 A | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| Oxygen Index | 20 % | 20 % | ASTM D2863 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 260 - 290 °C | 500 - 554 °F | |
| Mold Temperature | 70.0 - 90.0 °C | 158 - 194 °F |
|
上海松翰塑化科技有限公司，供应原料，品质真实,物实价廉。
PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。
欢迎各位客户前来咨询：
联系人： 夏先生
手 机：13501802636 021 51131842
QQ ：205730283
邮 箱 ：205730283@qq.com
主营系列:PC/ABS合金, PMMA亚克力, PPS聚苯硫醚, LCP液晶高分子聚合物, PPO聚苯醚,
PPA聚邻苯二甲酰胺耐高温尼龙, PEI聚醚酰亚胺 等原厂进口新料!
可提供原厂物性表，UL黄卡，COC，SGS等资料！欢迎来电咨询！联系QQ：205730283
手机：13751253137
类别：热塑性聚合物；聚合物；ABS；聚碳酸酯/ ABS合金，无筋；聚碳酸酯（PC）
材料说明：脉冲™a35-105工程树脂提供卓越的冲击强度即使在较低的温度和较高的热变形温度。