laripur lpr107 - 93a 物性及简介：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.19 g/cc | 1.19 g/cc | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 93 | 93 | ASTM D2240 |
| Tensile Strength, Yield | 57.7 MPa | 8370 psi | ASTM D412 |
| Elongation at Break | 550 % | 550 % | ASTM D412 |
| 50% Modulus | 0.00900 GPa | 1.31 ksi | ASTM D412 |
| 100% Modulus | 0.0108 GPa | 1.57 ksi | ASTM D412 |
| 300% Modulus | 0.0266 GPa | 3.86 ksi | ASTM D412 |
| Flexural Modulus | 0.0650 GPa | 9.43 ksi | ASTM D790 |
| Tear Strength | 122 kN/m | 696 pli | ASTM D624 |
| Abrasion | 35 | 35 | mm3, Abrasion Loss; DIN 53516 |
| Compression Set | 17 % | 17 % | 70 hours at 23°C; ASTM D395 |
| 18 % @Temperature 70.0 °C |
18 % @Temperature 158 °F |
Method B, 22 hours; ASTM D395 | |
| 38 % @Temperature 100 °C |
38 % @Temperature 212 °F |
70 hours; ASTM D395 | |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 175 °C | 347 °F | |
高分子热塑性；聚酯；聚氨酯，TP，TP；
材料：产品描述：笔记of the laripur®线是热塑性聚氨酯。这些产品的科技的结合热塑性聚氨酯制品with the特征：
优秀的磨损性能
在温度变化大的灵活性与constancy
好的压缩性
好水和光性
Good resistance to油，脂肪and to many types of溶剂
密封等级TPU产品：这些产品是specially developed for制造液gaskets or any other重负荷应用要求高压缩性，即使在高温和/或in contact with油和脂肪。两制品based on聚己内酯的聚酯，2202 - 95 and和107 93a，和一个基于PTMG聚醚和2203 - 93a。
上海松翰塑化科技有限公司供应产品，品质一流，TPV种类齐全。 公司理念你的要求就是我们的追求 。咨询人夏先生 电话：13751253137 QQ：205730283 我公司将给你最专业产品加工工艺指导及帮你解决加工工艺难题 欢迎你的咨询