颗粒原图类别：热塑性聚合物；聚合物；ABS；聚碳酸酯/ ABS合金，无筋；聚碳酸酯（PC）
材料说明：概述：脉冲2000工程树脂是专为在恶劣的应用提供最高的性能，从单件物品复杂的成分。理想的能源管理解决方案，它可以承受高温和低温、快速，重复的温度波动。
仪表板： 
膝 垫： 
内 饰：
上海松翰塑化科技有限公司，供应原料，品质真实,物实价廉。
PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。
欢迎各位客户前来咨询：
联系人： 夏先生
手 机：13501802636 021 51131842
QQ ：205730283
邮 箱 ：205730283@qq.com
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ASTM D792; ISO 1183/B |
| Water Absorption | 0.15 % @Temperature 23.0 °C, Time 86400 sec |
0.15 % @Temperature 73.4 °F, Time 24.0 hour |
ASTM D570; ISO 62 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ISO 294-4 |
| Melt Flow | 18 g/10 min | 18 g/10 min | ASTM D1238 |
| 18 g/10 min @Load 5.00 kg, Temperature 260 °C |
18 g/10 min @Load 11.0 lb, Temperature 500 °F |
ISO 1133 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 55.0 MPa | 7980 psi | 50 mm/min; ASTM D638 |
| 47.0 MPa @Thickness 4.00 mm |
6820 psi @Thickness 0.157 in |
Injection Molded; ISO 527-2/50 | |
| Tensile Strength, Yield | 58.0 MPa | 8410 psi | 50 mm/min; ASTM D638 |
| 57.0 MPa @Thickness 4.00 mm |
8270 psi @Thickness 0.157 in |
Injection Molded; ISO 527-2/50 | |
| Elongation at Break | 160 % | 160 % | ASTM D638 |
| 90 % @Thickness 4.00 mm |
90 % @Thickness 0.157 in |
Injection Molded; ISO 527-2/50 | |
| Elongation at Yield | 4.5 % @Thickness 4.00 mm |
4.5 % @Thickness 0.157 in |
Injection Molded; ISO 527-2/50 |
| Tensile Modulus | 2.33 GPa @Thickness 4.00 mm |
338 ksi @Thickness 0.157 in |
Injection Molded; ISO 527-2 |
| Flexural Strength | 90.0 MPa @Thickness 4.00 mm |
13100 psi @Thickness 0.157 in |
Injection Molded, 2 mm/min; ISO 178 |
| Flexural Modulus | 2.45 GPa | 355 ksi | 1.3 mm/min.; ASTM D790 |
| 2.40 GPa @Thickness 4.00 mm |
348 ksi @Thickness 0.157 in |
Injection Molded, 2 mm/min; ISO 178 | |
| Izod Impact, Notched (ISO) | 0.590 kJ/m² @Temperature -30.0 °C |
0.281 ft-lb/in² @Temperature -22.0 °F |
ASTM D256 |
| 0.750 kJ/m² @Temperature 23.0 °C |
0.357 ft-lb/in² @Temperature 73.4 °F |
ASTM D256 | |
| 47.0 kJ/m² @Temperature -30.0 °C |
22.4 ft-lb/in² @Temperature -22.0 °F |
ISO 180/A | |
| 63.0 kJ/m² @Temperature 23.0 °C |
30.0 ft-lb/in² @Temperature 73.4 °F |
ISO 180/A | |
| Dart Drop, Total Energy | 62.0 J | 45.7 ft-lb | 2.2 m/sec; ASTM D3763 |
| 55.0 J @Temperature 23.0 °C |
40.6 ft-lb @Temperature 73.4 °F |
2.2 m/sec; ASTM D3763 | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 109 °C | 228 °F | Unannealed; ASTM D648 |
| 130 °C | 266 °F | Unannealed; ISO 75-2/B | |
| Deflection Temperature at 1.8 MPa (264 psi) | 106 °C | 223 °F | Unannealed; ISO 75-2/A |
| Vicat Softening Point | 129 °C | 264 °F | ISO 306/B50 |
| 142 °C | 288 °F | ISO 306/A120 | |
| Flame Spread | <= 100 mm/min | <= 3.94 in/min | FMVSS 305 |