PC/ABS，聚碳酸酯和丙烯腈-丁二烯-苯乙烯共聚物和混合物，是由聚碳酸酯（Polycarbonate）和聚丙烯腈（ABS）合金而成的热可塑性塑胶，结合了两种材料的优异特性，ABS材料的成型性和PC的机械性、冲击强度和耐温、抗紫外线（UV）等性质，可广泛使用在汽车内部零件、事务机器、通信器材、家电用品及照明设备上。
典型应用范围:
汽车内外饰：仪表板，饰柱，仪表前盖，格栅，内外饰件 2.商务设备机壳和内置部件：笔记本/台式电脑，复印机，打印机，绘图仪，显示器 3.电信，移动电话外壳，附件以及智能卡（SIM卡）： 4.电器产品，电子产品外壳，电表罩和壳体，家用开关，插头和插座，电缆电线管道 5.家用电器，如洗衣机，吹风机，微波炉内外部件等。
等等、、参数：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ASTM D792; ISO 1183 |
| Water Absorption | 0.53 % @Temperature 23.0 °C, Time 86400 sec |
0.53 % @Temperature 73.4 °F, Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 6.0 g/10 min @Load 5.00 kg, Temperature 260 °C |
6.0 g/10 min @Load 11.0 lb, Temperature 500 °F |
ASTM D1238; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 53.0 MPa | 7690 psi | ISO 527-2 |
| 54.5 MPa | 7900 psi | ASTM D638 | |
| Tensile Strength, Yield | 51.0 MPa | 7400 psi | ASTM D638 |
| 54.0 MPa | 7830 psi | ISO 527-2 | |
| Elongation at Break | >= 80 % | >= 80 % | ISO 527-2; ASTM D638 |
| Elongation at Yield | 5.0 % | 5.0 % | ISO 527-2; ASTM D638 |
| Tensile Modulus | 2.16 GPa | 313 ksi | ASTM D638 |
| 2.28 GPa | 331 ksi | ISO 527-2 | |
| Flexural Strength | 68.0 MPa | 9860 psi | 3 points, 2 mm/min; ISO 178 |
| Flexural Modulus | 2.40 GPa | 348 ksi | 3 points, 2 mm/min; ISO 178 |
| Izod Impact, Notched | 6.40 J/cm @Temperature -40.0 °C |
12.0 ft-lb/in @Temperature -40.0 °F |
ASTM D256 |
| 7.50 J/cm @Temperature 23.0 °C |
14.1 ft-lb/in @Temperature 73.4 °F |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 61.0 kJ/m² @Temperature -40.0 °C |
29.0 ft-lb/in² @Temperature -40.0 °F |
ASTM D256 |
| 69.0 kJ/m² @Temperature 23.0 °C |
32.8 ft-lb/in² @Temperature 73.4 °F |
ASTM D256 | |
| Charpy Impact, Notched | 5.00 J/cm² @Temperature -40.0 °C |
23.8 ft-lb/in² @Temperature -40.0 °F |
ISO 179 |
| 6.10 J/cm² @Temperature 23.0 °C |
29.0 ft-lb/in² @Temperature 73.4 °F |
ISO 179 | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 74.0 µm/m-°C @Temperature -40.0 - 82.0 °C |
41.1 µin/in-°F @Temperature -40.0 - 180 °F |
ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C | 230 °F | Unannealed; ISO 75-2/B |
| 111 °C | 232 °F | Unannealed; ASTM D648 | |
| Vicat Softening Point | 130 °C | 266 °F | ISO 306/B50 |
| 144 °C | 291 °F | ISO 306/A120 |
|