与372有机玻璃的熔接性良好，制成双色塑件，且可表面镀铬，喷漆处理.有高抗冲、高耐热、阻燃、增强、透明等级别。流动性比HIPS差一点，比PMMA、PC等好，柔韧性好。
用途：
适于制作一般机械零件，减磨耐磨零件，传动零件和电讯零件.
用途：
适于制作一般机械零件，减磨耐磨零件，传动零件和电讯零件.
同PVC（聚氯乙烯）一样在屈折处会出现白化现象。
参数：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.44 g/cc | 0.0520 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 121 | 121 | ASTM D785 |
| Tensile Strength, Yield | 100 MPa | 14500 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Yield Strength | 155 MPa | 22500 psi | ASTM D790 |
| Flexural Modulus | 7.30 GPa | 1060 ksi | ASTM D790 |
| Izod Impact, Notched | 0.900 J/cm | 1.69 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 131 °C | 268 °F | ASTM D648 |
| Flammability, UL94 | V-0 | V-0 | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 230 - 300 °C | 446 - 572 °F | |
| Mold Temperature | 70.0 - 110 °C | 158 - 230 °F | |