| Gichem GIBLEND E45X3/VO ABS - Polycarbonate - PC/ABS Flame Retardant 1、综合性能较好，冲击强度较高，化学稳定性，电性能良好. 2、与372有机玻璃的熔接性良好，制成双色塑件，且可表面镀铬，喷漆处理. 3、有高抗冲、高耐热、阻燃、增强、透明等级别。 4、流动性比HIPS差一点，比PMMA、PC等好，柔韧性好。 5、用途：适于制作一般机械零件，减磨耐磨零件，传动零件和电讯零件. 6、同PVC（聚氯乙烯）一样在屈折处会出现白化现象。 |
图样| 参数： | |||
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in³ | ASTM D792 |
| Water Absorption | 0.20 % | 0.20 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 15 g/10 min | 15 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | ASTM D638 |
| Elongation at Yield | 30 % | 30 % | ASTM D638 |
| Flexural Modulus | 2.40 GPa | 348 ksi | ASTM D790 |
| Izod Impact, Notched | 3.50 J/cm | 6.56 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 96.0 °C | 205 °F | ASTM D648 |
| Vicat Softening Point | 108 °C | 226 °F | ASTM D1525/A |
| Flammability, UL94 | V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
|
| V-0 @Thickness 3.20 mm |
V-0 @Thickness 0.126 in |
||
| Oxygen Index | 32 % | 32 % | ASTM D2863 |
| Glow Wire Test | 960 °C | 1760 °F | IEC 695-2-1 |
| Processing Properties | Metric | English | Comments |
| Middle Barrel Temperature | 220 - 240 °C | 428 - 464 °F | |
| Mold Temperature | 50.0 - 70.0 °C | 122 - 158 °F | |
| Drying Temperature | 100 °C | 212 °F | 2 hours |