类别：高分子聚合物；热凝；ABS；聚碳酸酯/ ABS合金，unreinforced聚碳酸酯（PC）；
材料：ABS共混PC笔记自我灭火级V0高流动性。培养基注射速度。
PC/ABS比重:1.05克/立方厘米
燃烧鉴别方法：连续燃烧、蓝底黄火焰、黑烟、浅金盏草味
溶剂实验：环已酮可软化，芳香溶剂无作用
| 参数： | |||
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ASTM D792 |
| Water Absorption | 0.20 % | 0.20 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 20 g/10 min | 20 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | ASTM D638 |
| Elongation at Yield | 45 % | 45 % | ASTM D638 |
| Flexural Modulus | 2.45 GPa | 355 ksi | ASTM D790 |
| Izod Impact, Notched | 4.50 J/cm | 8.43 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C | 230 °F | ASTM D648 |
| Vicat Softening Point | 115 °C | 239 °F | ASTM D1525/A |
| Flammability, UL94 | V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
|
| V-0 @Thickness 3.20 mm |
V-0 @Thickness 0.126 in |
||
| Flammability Test | 125 | 125 | [°C] Bilia; IEC 331 |
| Oxygen Index | 32 % | 32 % | ASTM D2863 |
| Glow Wire Test | 960 °C | 1760 °F | IEC 695-2-1 |
| Processing Properties | Metric | English | Comments |
| Middle Barrel Temperature | 230 - 250 °C | 446 - 482 °F | |
| Mold Temperature | 50.0 - 70.0 °C | 122 - 158 °F | |
| Drying Temperature | 100 °C | 212 °F | 2 hours |