如图材料注意事项：
特征：
UL HB @ 1.6-3.2mm
出色的平衡性能
高刚度
尺寸稳定性好
良好的表面粘附
优良的加工性能，大部分
应用：
注射成型
汽车仪表板
光盘库提取
| 参数： | |||||
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.22 g/cc @Temperature 23.0 °C |
1.22 g/cc @Temperature 73.4 °F |
ASTM D792 | ||
| Water Absorption | 0.12 % @Temperature 23.0 °C, Time 86400 sec |
0.12 % @Temperature 73.4 °F, Time 24.0 hour |
ASTM D570 | ||
| Linear Mold Shrinkage | 0.0030 - 0.0050 cm/cm @Temperature 23.0 °C |
0.0030 - 0.0050 in/in @Temperature 73.4 °F |
ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 82 | 82 | ASTM D785 | ||
| Tensile Strength at Break | 76.0 MPa | 11000 psi | 10mm/min; ASTM D638 | ||
| Elongation at Break | 7.0 % | 7.0 % | 10mm/min; ASTM D638 | ||
| Flexural Strength | 119 MPa | 17300 psi | 2mm/min; ASTM D790 | ||
| Flexural Modulus | 4.35 GPa | 631 ksi | 2mm/min; ASTM D790 | ||
| Izod Impact, Notched | 0.750 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
1.41 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 | ||
| Izod Impact, Unnotched | 2.80 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
5.25 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 | ||
| Surface Resistance | 1.00e+16 ohm | 1.00e+16 ohm | ASTM D257 | ||
| Dielectric Strength | 28.0 kV/mm | 711 kV/in | 1.6mm; ASTM D149 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 130 °C @Thickness 6.40 mm |
266 °F @Thickness 0.252 in |
ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 120 °C @Thickness 6.40 mm |
248 °F @Thickness 0.252 in |
ASTM D648 | ||
| Flammability, UL94 | HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
|||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | <= 285 °C | <= 545 °F | |||
| Rear Barrel Temperature | 240 - 260 °C | 464 - 500 °F | Start Point: 250°C | ||
| Middle Barrel Temperature | 245 - 270 °C | 473 - 518 °F | Start Point: 255°C | ||
| Front Barrel Temperature | 250 - 280 °C | 482 - 536 °F | Start Point: 260°C | ||
| Melt Temperature | 240 - 270 °C | 464 - 518 °F | Start Point: 260°C | ||
| Mold Temperature | 80.0 - 130 °C | 176 - 266 °F | Start Point: 90°C | ||
| Drying Temperature | 100 - 110 °C @Time 14400 - 21600 sec |
212 - 230 °F @Time 4.00 - 6.00 hour |
Pre-dry | ||
| Back Pressure | 0.000 - 0.700 MPa | 0.000 - 102 psi | |||
| De |
|||||
| Glass Fiber Content (%) | 10 | ||||
| Injection Speed | 60-90% | ||||