| 类别： | 热塑性聚合物；聚合物；ABS；聚碳酸酯/ ABS合金，玻璃纤维填充；聚碳酸酯（PC） |
| 材料注意事项： |
|
图
图| 参数： | |||||
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.42 g/cc @Temperature 23.0 °C |
1.42 g/cc @Temperature 73.4 °F |
ASTM D792 | ||
| Water Absorption | 0.10 % @Temperature 23.0 °C, Time 86400 sec |
0.10 % @Temperature 73.4 °F, Time 24.0 hour |
ASTM D570 | ||
| Linear Mold Shrinkage | 0.0020 - 0.0040 cm/cm @Temperature 23.0 °C |
0.0020 - 0.0040 in/in @Temperature 73.4 °F |
ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 84 | 84 | ASTM D785 | ||
| Tensile Strength at Break | 108 MPa | 15700 psi | 10mm/min; ASTM D638 | ||
| Elongation at Break | 6.0 % | 6.0 % | 10mm/min; ASTM D638 | ||
| Flexural Strength | 148 MPa | 21500 psi | 2mm/min; ASTM D790 | ||
| Flexural Modulus | 9.30 GPa | 1350 ksi | 2mm/min; ASTM D790 | ||
| Izod Impact, Notched | 0.850 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
1.59 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 | ||
| Izod Impact, Unnotched | 3.80 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
7.12 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 | ||
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | ASTM D257 | ||
| Dielectric Strength | 29.0 kV/mm | 737 kV/in | 1.6mm; ASTM D149 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 128 °C @Thickness 6.40 mm |
262 °F @Thickness 0.252 in |
ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 115 °C @Thickness 6.40 mm |
239 °F @Thickness 0.252 in |
ASTM D648 | ||
| Flammability, UL94 | V-0 @Thickness 3.20 mm |
V-0 @Thickness 0.126 in |
|||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | <= 255 °C | <= 491 °F | |||
| Rear Barrel Temperature | 220 - 240 °C | 428 - 464 °F | Start Point: 230°C | ||
| Middle Barrel Temperature | 225 - 240 °C | 437 - 464 °F | Start Point: 230°C | ||
| Front Barrel Temperature | 240 - 250 °C | 464 - 482 °F | Start Point: 240°C | ||
| Melt Temperature | 230 - 250 °C | 446 - 482 °F | Start Point: 240°C | ||
| Mold Temperature | 80.0 - 110 °C | 176 - 230 °F | Start Point: 90°C | ||
| Drying Temperature | 100 - 110 °C @Time 14400 - 21600 sec |
212 - 230 °F @Time 4.00 - 6.00 hour |
Pre-dry | ||
| Back Pressure | 0.000 - 1.00 MPa | 0.000 - 145 psi | |||
| De |
|||||
| Glass Fiber Content (%) | 30 | ||||
| Injection Speed | 50-90% | ||||