PC/ABS, HG5000B Resistance_产品资讯

HG5000B Heat Resistance PC/ABS：

　　1、综合性能较好,冲击强度较高,化学稳定性,电性能良好.

　　2、与372有机玻璃的熔接性良好,制成双色塑件,且可表面镀铬,喷漆处理.

　　3、有高抗冲、高耐热、阻燃、增强、透明等级别。

　　4、流动性比HIPS差一点，比PMMA、PC等好，柔韧性好。

典型应用范围:手机外壳、计算机和商业机器壳体、电器设备、草坪园艺机器、汽车零件仪表板、内部装修以及车轮盖）。

本公司承诺:所销售之塑胶原料均为进口原厂原包材料、均可提供原厂的物性表，UL MSDS SGS COC 欢迎来电咨询！

本公司长期供应各大工厂的工程塑料及通用塑料，例如：杜邦.巴塞尔.菲利普.宝理.东丽.DIC.出光.巴斯夫.等等.欢迎来电咨询，采购。

提供物性表；

Physical Properties	Metric	English	Comments

Specific Gravity	1.14 g/cc	1.14 g/cc	ASTM D792
Maximum Moisture Content	0.020	0.020	Injection Molding
Linear Mold Shrinkage, Flow	0.0050 - 0.0080 cm/cm @Thickness 3.20 mm	0.0050 - 0.0080 in/in @Thickness 0.126 in	ASTM D955
Melt Flow	7.5 g/10 min @Load 2.16 kg, Temperature 250 °C	7.5 g/10 min @Load 4.76 lb, Temperature 482 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	116	116	ASTM D785
Tensile Strength, Yield	59.8 MPa @Thickness 3.20 mm	8680 psi @Thickness 0.126 in	50mm/min; ASTM D638
Elongation at Break	>= 100 % @Thickness 3.20 mm	>= 100 % @Thickness 0.126 in	50mm/min; ASTM D638
Flexural Yield Strength	91.2 MPa @Thickness 3.20 mm	13200 psi @Thickness 0.126 in	10mm/min; ASTM D790
Flexural Modulus	2.26 GPa @Thickness 3.20 mm	327 ksi @Thickness 0.126 in	10mm/min; ASTM D790
Izod Impact, Notched	>= 5.49 J/cm @Thickness 3.20 mm, Temperature 23.0 °C	>= 10.3 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F	ASTM D256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	114 °C @Thickness 6.40 mm	237 °F @Thickness 0.252 in	Unannealed; ASTM D648
UL RTI, Electrical	60.0 °C @Thickness >=1.50 mm	140 °F @Thickness >=0.0591 in
	60.0 °C @Thickness >=3.00 mm	140 °F @Thickness >=0.118 in
UL RTI, Mechanical with Impact	60.0 °C @Thickness >=1.50 mm	140 °F @Thickness >=0.0591 in
	60.0 °C @Thickness >=3.00 mm	140 °F @Thickness >=0.118 in
UL RTI, Mechanical without Impact	60.0 °C @Thickness >=1.50 mm	140 °F @Thickness >=0.0591 in
	60.0 °C @Thickness >=3.00 mm	140 °F @Thickness >=0.118 in
Flammability, UL94	HB @Thickness >=1.50 mm	HB @Thickness >=0.0591 in
	HB @Thickness >=3.00 mm	HB @Thickness >=0.118 in

Processing Properties	Metric	English	Comments
Rear Barrel Temperature	240 - 270 °C	464 - 518 °F	Injection Molding
Middle Barrel Temperature	245 - 275 °C	473 - 527 °F	Injection Molding
Front Barrel Temperature	245 - 275 °C	473 - 527 °F	Injection Molding
Nozzle Temperature	245 - 275 °C	473 - 527 °F	Injection Molding
Melt Temperature	250 - 275 °C	482 - 527 °F	Injection Molding
Mold Temperature	50.0 - 70.0 °C	122 - 158 °F	Injection Molding
Drying Temperature	80.0 - 100 °C	176 - 212 °F	Injection Molding
Dry Time	4.00 - 6.00 hour	4.00 - 6.00 hour	Injection Molding
Screw Speed	40 - 70 rpm	40 - 70 rpm	Injection Molding