颗粒图片
包装库存
产品应用展示图
TPV 123-50 物性表：
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 0.960 g/cc | 0.960 g/cc | 23°C; ASTM D792 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 43 | 43 | Air at 302°F, 168 hr; ASTM D573 | ||
| 41 @Thickness 2.00 mm, Time 15.0 sec |
41 @Thickness 0.0787 in, Time 0.00417 hour |
ISO 868 | |||
| Tensile Strength at Break | 15.85 MPa | 2299 psi | Air at 302°F, 168 hr; ASTM D573 | ||
| 19.1 MPa | 2770 psi | Across Flow; ASTM D412 | |||
| Tensile Stress | 9.10 MPa @Strain 100 % |
1320 psi @Strain 100 % |
Across Flow; ASTM D412 | ||
| Elongation at Break | 483.6 % | 483.6 % | Air at 302°F, 168 hr; ASTM D573 | ||
| 620 % | 620 % | Across Flow; ASTM D412 | |||
| Tear Strength | 67.1 kN/m | 383 pli | 73°F, Die C, Across Flow; ASTM D624 | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Constant | 2.6 | 2.6 | 1.98 mm; ASTM D150 | ||
| Dielectric Strength | 31.1 kV/mm | 790 kV/in | 2.03 mm; ASTM D149 | ||
| Thermal Properties | Metric | English | Comments | ||
| Brittleness Temperature | -57.8 °C | -72.0 °F | ASTM D746 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 175 - 230 °C | 347 - 446 °F | |||
| Rear Barrel Temperature | 193 °C | 380 °F | |||
| Middle Barrel Temperature | 199 °C | 390 °F | |||
| Front Barrel Temperature | 204 °C | 400 °F | |||
| Nozzle Temperature | 210 - 238 °C | 410 - 460 °F | |||
| Die Temperature | 216 °C | 420 °F | Extrusion | ||
| Melt Temperature | 210 °C | 410 °F | Extrusion | ||
| 216 - 232 °C | 420 - 450 °F | Processing | |||
| Mold Temperature | 10.0 - 51.7 °C | 50.0 - 125 °F | Processing | ||
| Drying Temperature | 82.2 °C | 180 °F | |||
| Dry Time | 3 hour | 3 hour | |||
| Moisture Content | 0.080 % | 0.080 % | |||
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 100 psi | Processing | ||
| 5.00 - 20.0 MPa | 725 - 2900 psi | Extrusion | |||
| Clamp Pressure | 41.4 - 68.9 MPa | 6000 - 10000 psi | |||
| Vent Depth | 0.00254 cm | 0.00100 in | |||
| Cushion | 0.317 - 0.635 cm | 0.125 - 0.250 in | |||
| Screw Speed | 100 - 200 rpm | 100 - 200 rpm | |||
| De |
|||||
| Color | Black | ||||
| Form | Pellets | ||||
| Injection Rate | Fast | ||||
| Maximum Regrind % | 20 | ||||
| Screw Compression Ratio | 2:1 - 2.5:1 | ||||
| Screw L/D Ratio | 16:1 - 20:1 |
||||
1、 优异的抗老化性能和良好的耐候、耐热性能；
2、 优异的抗永久变形性能；
3、 优异的抗张强度、高韧性和高回弹性；
4、 优异的环保性能和可重复使用；
5、 优异的电绝缘性能；
6、 硬度范围广泛；
7、 使用温度范围广泛；
8、 颜色多样化，有全透明、半透明、浅色系列，着色容易，容易加工成型；
9、 可与PP、PA、PC、ABS、PS、PBT、PET等多种材料共注射或挤出成型。
广泛应用于：电子产品外壳及外保护、建筑材料密封条、交通器材缓冲部件、消费品的主体如鱼竿牙刷吸管等、、、、、