TPU 78 E 4588 物性表：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Flow | 14 g/10 min @Load 3.80 kg, Temperature 190 °C |
14 g/10 min @Load 8.38 lb, Temperature 374 °F |
ASTM D1238 |
| 52.53 g/10 min @Load 8.70 kg, Temperature 190 °C |
52.53 g/10 min @Load 19.2 lb, Temperature 374 °F |
ASTM D1238 | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 66 | 66 | 5 sec. delay; ASTM D2240 |
| Tensile Strength, Ultimate | 24.3 MPa | 3520 psi | 10 in/min; ASTM D412 |
| Elongation at Break | 772 % | 772 % | 10 in/min; ASTM D412 |
| 50% Modulus | 0.00188 GPa | 0.273 ksi | 10 in/min; ASTM D412 |
| 100% Modulus | 0.00245 GPa | 0.355 ksi | ISO 37 |
| 200% Modulus | 0.00315 GPa | 0.457 ksi | 10 in/min; ASTM D412 |
| 300% Modulus | 0.00405 GPa | 0.587 ksi | 10 in/min; ASTM D412 |
| Tear Strength | 53.8 kN/m | 307 pli | Die 'C' Tear; 20 in/min; ASTM D624 |
| Compression Set | 26.9 % | 26.9 % | 23°C, 22 hrs.; ASTM D395 |
| 68 % @Temperature 70.0 °C |
68 % @Temperature 158 °F |
22 hrs; ASTM D395 | |
| Tensile Set | 12.6 % | 12.6 % | 23°C, 22 hrs.; at 100% per ASTM D412 |
高耐磨性:硬度范围广：通过改变/TPU各反应组分的配比，可以得到不同硬度的产品，而且随着硬度的增加,其产品仍保持良好的弹性/机械强度高：制品的承载能力、抗冲击性及减震性能突出、耐寒性突出：TPU的玻璃态转变温度比较低，在零下35度仍保持良好的弹性、柔顺性和其他物理性能、加工性能好、TPU可采用常见的热塑性材料的加工方法进行加工，
可采用常见的热塑性材料的加工方法进行加工,如注射、挤出、压延等等、同时，TPU与某些高分子材料共同加工能够得到性能互补的聚合物合金、耐油、耐水、耐霉菌、在生利用性好。
应用领域：
1.鞋类：运动鞋Logo、运动鞋气垫、登山鞋、雪鞋、高尔夫球鞋、溜冰鞋、之面料及内里贴合材料。
2.成衣类：雪衣、雨衣、风衣、防寒夹克、野战服、纸尿裤、 生理裤、等面料复合材料(防水透湿)。
3医药类：手术衣、帽、鞋、 医院用褥垫、冰袋、绷带、血浆袋、外科用包扎布条、口罩、等面料及内里材料，手术床气囊。
4国防用品：飞机油箱，武器封存覆膜、帐棚窗口、军用水袋、救生衣，充汽艇等之面料及内里面料，气囊。
5.运动用品：足球表面及内胆、充气床、饮水袋、滑雪手套(防水袋)、潜水衣、雪衣、泳装、滑雪板、商标、气囊、运动衫、瘦身衣等面料及内里材料。