TPU 92 E 4694物性表:
Physical Properties | Metric | English | Comments | ||
---|---|---|---|---|---|
Density | 1.21 g/cc | 0.0437 lb/in³ | ASTM D792 | ||
Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | ASTM D995 | ||
Melt Index of Compound | 57 g/10 min @Load 10.0 kg, Temperature 210 °C |
57 g/10 min @Load 22.0 lb, Temperature 410 °F |
cm3/10 min | ||
Mechanical Properties | Metric | English | Comments | ||
Hardness, Shore A | 92 | 92 | ASTM D2240 | ||
Hardness, Shore D | 41 | 41 | ASTM D2240 | ||
Tensile Strength at Break | 55.0 MPa | 7980 psi | DIN 53504 | ||
Elongation at Break | 570 % | 570 % | ASTM D412 | ||
100% Modulus | 0.00820 GPa | 1.19 ksi | DIN 53504 | ||
300% Modulus | 0.0197 GPa | 2.86 ksi | DIN 53504 | ||
Rebound | 32 % | 32 % | Bayshore; ASTM D2632 | ||
Tear Strength | 137 kN/m | 780 pli | ASTM D624 | ||
Abrasion | 35 | 35 | [mm3]; ISO 4649 | ||
Compression Set | 23 % @Temperature 23.0 °C, Time 252000 sec |
23 % @Temperature 73.4 °F, Time 70.0 hour |
ASTM D395 | ||
40 % @Temperature 70.0 °C, Time 86400 sec |
40 % @Temperature 158 °F, Time 24.0 hour |
ASTM D395 | |||
Thermal Properties | Metric | English | Comments | ||
Melting Point | 160 - 190 °C | 320 - 374 °F | Huntsman/TMA | ||
Optical Properties | Metric | English | Comments | ||
Transmission, Visible | 90 % | 90 % | transparent; thickness not reported | ||
Processing Properties | Metric | English | Comments | ||
Feed Temperature | 25.0 - 40.0 °C | 77.0 - 104 °F | Extrusion | ||
Front Barrel Temperature | 165 - 190 °C | 329 - 374 °F | Extrusion | ||
Nozzle Temperature | 170 - 200 °C | 338 - 392 °F | Extrusion | ||
180 - 200 °C | 356 - 392 °F | Injection | |||
Adapter Temperature | 175 - 195 °C | 347 - 383 °F | Extrusion | ||
Die Temperature | 175 - 200 °C | 347 - 392 °F | Extrusion | ||
Melt Temperature | 170 - 195 °C | 338 - 383 °F | Injection | ||
Mold Temperature | 20.0 - 70.0 °C | 68.0 - 158 °F | Injection | ||
De |
|||||
Heating Zone | 175-195°C |
高耐磨性:硬度范围广:通过改变/TPU各反应组分的配比,可以得到不同硬度的产品,而且随着硬度的增加,其产品仍保持良好的弹性/机械强度高:制品的承载能力、抗冲击性及减震性能突出、耐寒性突出:TPU的玻璃态转变温度比较低,在零下35度仍保持良好的弹性、柔顺性和其他物理性能、加工性能好、TPU可采用常见的热塑性材料的加工方法进行加工,
可采用常见的热塑性材料的加工方法进行加工,如注射、挤出、压延等等、同时,TPU与某些高分子材料共同加工能够得到性能互补的聚合物合金、耐油、耐水、耐霉菌、在生利用性好。
应用领域:
1.鞋类:运动鞋Logo、运动鞋气垫、登山鞋、雪鞋、高尔夫球鞋、溜冰鞋、之面料及内里贴合材料。
2.成衣类:雪衣、雨衣、风衣、防寒夹克、野战服、纸尿裤、 生理裤、等面料复合材料(防水透湿)。
3医药类:手术衣、帽、鞋、 医院用褥垫、冰袋、绷带、血浆袋、外科用包扎布条、口罩、等面料及内里材料,手术床气囊。
4国防用品:飞机油箱,武器封存覆膜、帐棚窗口、军用水袋、救生衣,充汽艇等之面料及内里面料,气囊。
5.运动用品:足球表面及内胆、充气床、饮水袋、滑雪手套(防水袋)、潜水衣、雪衣、泳装、滑雪板、商标、气囊、运动衫、瘦身衣等面料及内里材料。
上海松翰塑化科技有限公司供应产品,品质一流,TPV种类齐全。 公司理念你的要求就是我们的追求 。咨询人夏先生 电话:13751253137 QQ:205730283 我公司将给你最专业产品加工工艺指导及帮你解决加工工艺难题 欢迎你的咨询