特点：
1、综合性能较好，冲击强度较高，化学稳定性，电性能良好.
2、与372有机玻璃的熔接性良好，制成双色塑件，且可表面镀铬，喷漆处理.
3、有高抗冲、高耐热、阻燃、增强、透明等级别。
4、流动性比HIPS差一点，比PMMA、PC等好，柔韧性好。
5、用途：适于制作一般机械零件，减磨耐磨零件，传动零件和电讯零件.
6、同PVC（聚氯乙烯）一样在屈折处会出现白化现象。
| 物性表： | |||||
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.19 g/cc | 1.19 g/cc | ASTM D792 | ||
| Density | 1.18 g/cc | 0.0426 lb/in³ | ISO 1183 | ||
| 1.20 g/cc | 0.0434 lb/in³ | ISO 1183 | |||
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm @Thickness 3.20 mm |
0.0030 - 0.0050 in/in @Thickness 0.126 in |
SABIC Method | ||
| Melt Flow | 14 g/10 min @Load 2.16 kg, Temperature 260 °C |
14 g/10 min @Load 4.76 lb, Temperature 500 °F |
ASTM D1238 | ||
| Melt Index of Compound | 14 g/10 min @Load 2.16 kg, Temperature 260 °C |
14 g/10 min @Load 4.76 lb, Temperature 500 °F |
MVR [cm^3/10 min]; ISO 1133 | ||
| 22 g/10 min @Load 5.00 kg, Temperature 260 °C |
22 g/10 min @Load 11.0 lb, Temperature 500 °F |
MVR [cm^3/10 min]; ISO 1133 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 121 | 121 | ISO 2039-2 | ||
| Hardness, H358/30 | 99.0 MPa | 14400 psi | ISO 2039-1 | ||
| Tensile Strength at Break | 45.0 MPa | 6530 psi | 50 mm/min; ISO 527 | ||
| 46.0 MPa | 6670 psi | Type I, 50 mm/min; ASTM D638 | |||
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | 50 mm/min; ISO 527 | ||
| 59.0 MPa | 8560 psi | Type I, 50 mm/min; ASTM D638 | |||
| Elongation at Break | 15 % | 15 % | 50 mm/min; ISO 527 | ||
| 20 % | 20 % | Type I, 50 mm/min; ASTM D638 | |||
| Elongation at Yield | 4.0 % | 4.0 % | Type I, 50 mm/min; ASTM D638 | ||
| 5.0 % | 5.0 % | 50 mm/min; ISO 527 | |||
| Tensile Modulus | 2.40 GPa | 348 ksi | 1 mm/min; ISO 527 | ||
| 3.10 GPa | 450 ksi | 50 mm/min; ASTM D638 | |||
| Flexural Yield Strength | 82.0 MPa | 11900 psi | 2 mm/min; ISO 178 | ||
| 94.0 MPa | 13600 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |||
| Flexural Modulus | 2.40 GPa | 348 ksi | 2 mm/min; ISO 178 | ||
| 2.68 GPa | 389 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |||
| Izod Impact, Notched | 1.60 J/cm | 3.00 ft-lb/in | ASTM D256 | ||
| Izod Impact, Notched (ISO) | 24.0 kJ/m² | 11.4 ft-lb/in² | 80*10*4; ISO 180/1A | ||
| 12.0 kJ/m² @Temperature -30.0 °C |
5.71 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |||
| Charpy Impact, Notched | 2.50 J/cm² | 11.9 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA | ||
| 1.30 J/cm² @Temperature -30.0 °C |
6.19 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eA | |||
| Dart Drop, Total Energy | 47.0 J @Temperature 23.0 °C |
34.7 ft-lb @Temperature 73.4 °F |
ASTM D3763 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 | ||
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | ROA; IEC 60093 | ||
| Dielectric Constant | 2.7 @Frequency 1.00e+6 Hz |
2.7 @Frequency 1.00e+6 Hz |
IEC 60250 | ||
| 2.8 @Frequency 50.0 - 60.0 Hz |
2.8 @Frequency 50.0 - 60.0 Hz |
IEC 60250 | |||
| Dielectric Strength | 17.0 kV/mm @Thickness 3.20 mm |
432 kV/in @Thickness 0.126 in |
in oil; IEC 60243-1 | ||
| 25.0 kV/mm @Thickness 1.60 mm |
635 kV/in @Thickness 0.0630 in |
in oil; IEC 60243-1 | |||
| 35.0 kV/mm @Thickness 0.800 mm |
889 kV/in @Thickness 0.0315 in |
in oil; IEC 60243-1 | |||
| Dissipation Factor | 0.0030 @Frequency 50.0 - 60.0 Hz |
0.0030 @Frequency 50.0 - 60.0 Hz |
IEC 60250 | ||
| 0.0050 @Frequency 1.00e+6 Hz |
0.0050 @Frequency 1.00e+6 Hz |
IEC 60250 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 72.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
40.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | ||
| 80.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
44.4 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 | |||
| CTE, linear, Transverse to Flow | 72.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
40.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | ||
| 80.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
44.4 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 | |||
| Thermal Conductivity | 0.200 W/m-K | 1.39 BTU-in/hr-ft²-°F | ISO 8302 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 128 °C | 262 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be | ||
| 90.0 °C @Thickness 3.20 mm |
194 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 108 °C | 226 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae | ||
| 82.0 °C @Thickness 3.20 mm |
180 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |||
| Vicat Softening Point | 98.0 °C | 208 °F | Rate B/50; ASTM D1525 | ||
| 128 °C | 262 °F | Rate B/50; ISO 306 | |||
| 130 °C | 266 °F | Rate B/120; ISO 306 | |||
| UL RTI, Electrical | 60.0 °C | 140 °F | UL 746B | ||
| UL RTI, Mechanical with Impact | 60.0 °C | 140 °F | UL 746B | ||
| UL RTI, Mechanical without Impact | 60.0 °C | 140 °F | UL 746B | ||
| Flammability, UL94 | V-2 @Thickness 1.01 mm |
V-2 @Thickness 0.0398 in |
UL 94 | ||
| V-1 @Thickness 1.19 mm |
V-1 @Thickness 0.0469 in |
UL 94 | |||
| V-0 @Thickness 1.49 mm |
V-0 @Thickness 0.0587 in |
UL 94 | |||
| 5VB @Thickness 2.00 mm |
5VB @Thickness 0.0787 in |
UL 94 | |||
| Oxygen Index | 23 % | 23 % | ISO 4589 | ||
| De |
|||||
| Ball Pressure Test, 125°C +/- 2°C | PASSES | IEC 60695-10-2 |
|||
典型应用范围:
汽车内外饰：仪表板，饰柱，仪表前盖，格栅，内外饰件 2.商务设备机壳和内置部件：笔记本/台式电脑，复印机，打印机，绘图仪，显示器 3.电信，移动电话外壳，附件以及智能卡（SIM卡）： 4.电器产品，电子产品外壳，电表罩和壳体，家用开关，插头和插座，电缆电线管道 5.家用电器，如洗衣机，吹风机，微波炉内外部件等。