TPU 85 P 4394 物性表：
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in³ | ASTM D792 | ||
| Linear Mold Shrinkage | 0.010 cm/cm | 0.010 in/in | ASTM D995 | ||
| Melt Flow | 30 - 60 g/10 min | 30 - 60 g/10 min | Melt Volume Rate (cm³/10 min) | ||
| Melt Index of Compound | 50 g/10 min @Load 21.6 kg, Temperature 190 °C |
50 g/10 min @Load 47.6 lb, Temperature 374 °F |
cm3/10 min | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 86 | 86 | ASTM D2240 | ||
| Hardness, Shore D | 35 | 35 | ASTM D2240 | ||
| Tensile Strength at Break | 40.0 MPa | 5800 psi | DIN 53504 | ||
| Elongation at Break | 660 % | 660 % | ASTM D412 | ||
| 100% Modulus | 0.00650 GPa | 0.943 ksi | DIN 53504 | ||
| 300% Modulus | 0.0102 GPa | 1.48 ksi | DIN 53504 | ||
| Rebound | 42 % | 42 % | Bayshore; ASTM D2632 | ||
| Tear Strength | 85.9 kN/m | 490 pli | ASTM D624 | ||
| Abrasion | 35 | 35 | [mm3]; ISO 4649 | ||
| Compression Set | 22 % @Temperature 23.0 °C, Time 252000 sec |
22 % @Temperature 73.4 °F, Time 70.0 hour |
ASTM D395 | ||
| 40 % @Temperature 70.0 °C, Time 86400 sec |
40 % @Temperature 158 °F, Time 24.0 hour |
ASTM D395 | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 171 - 190 °C | 340 - 374 °F | Huntsman/TMA | ||
| Flammability, UL94 | V-2 | V-2 | Non-Halogen FR | ||
| Processing Properties | Metric | English | Comments | ||
| Feed Temperature | 25.0 - 40.0 °C | 77.0 - 104 °F | Extrusion | ||
| Front Barrel Temperature | 165 - 190 °C | 329 - 374 °F | Extrusion | ||
| Nozzle Temperature | 170 - 200 °C | 338 - 392 °F | Extrusion | ||
| 180 - 200 °C | 356 - 392 °F | Injection | |||
| Adapter Temperature | 175 - 195 °C | 347 - 383 °F | Extrusion | ||
| Die Temperature | 175 - 200 °C | 347 - 392 °F | Extrusion | ||
| Melt Temperature | 170 - 195 °C | 338 - 383 °F | Injection | ||
| Mold Temperature | 20.0 - 70.0 °C | 68.0 - 158 °F | Injection | ||
| De |
|||||
| Heating Zone | 175-195°C |
||||
高耐磨性:硬度范围广：通过改变/TPU各反应组分的配比，可以得到不同硬度的产品，而且随着硬度的增加,其产品仍保持良好的弹性/机械强度高：制品的承载能力、抗冲击性及减震性能突出、耐寒性突出：TPU的玻璃态转变温度比较低，在零下35度仍保持良好的弹性、柔顺性和其他物理性能、加工性能好、TPU可采用常见的热塑性材料的加工方法进行加工，
可采用常见的热塑性材料的加工方法进行加工,如注射、挤出、压延等等、同时，TPU与某些高分子材料共同加工能够得到性能互补的聚合物合金、耐油、耐水、耐霉菌、在生利用性好。
优良的抗微生物性，高低温适应性，特别适用于电缆护套及软管类产品。
上海松翰塑化科技有限公司供应产品，品质一流，TPV种类齐全。 公司理念你的要求就是我们的追求 。咨询人夏先生 电话：13751253137 QQ：205730283 我公司将给你最专业产品加工工艺指导及帮你解决加工工艺难题 欢迎你的咨询