特点：
1、综合性能较好，冲击强度较高，化学稳定性，电性能良好.
2、与372有机玻璃的熔接性良好，制成双色塑件，且可表面镀铬，喷漆处理.
3、有高抗冲、高耐热、阻燃、增强、透明等级别。
4、流动性比HIPS差一点，比PMMA、PC等好，柔韧性好。
5、用途：适于制作一般机械零件，减磨耐磨零件，传动零件和电讯零件.
6、同PVC（聚氯乙烯）一样在屈折处会出现白化现象。
典型应用范围:
汽车内外饰：仪表板，饰柱，仪表前盖，格栅，内外饰件 2.商务设备机壳和内置部件：笔记本/台式电脑，复印机，打印机，绘图仪，显示器 3.电信，移动电话外壳，附件以及智能卡（SIM卡）： 4.电器产品，电子产品外壳，电表罩和壳体，家用开关，插头和插座，电缆电线管道 5.家用电器，如洗衣机，吹风机，微波炉内外部件等。
| 物性表: | |||
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.13 g/cc | 1.13 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0050 cm/cm @Thickness 3.20 mm |
0.0050 in/in @Thickness 0.126 in |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm @Thickness 3.20 mm |
0.0070 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 30 g/10 min @Load 10.0 kg, Temperature 250 °C |
30 g/10 min @Load 22.0 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 111 | 111 | ASTM D785 |
| Tensile Strength at Break | 48.8 MPa | 7080 psi | 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 49.0 MPa | 7110 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | 100 % | 100 % | 50 mm/min; ASTM D638 |
| Tensile Modulus | 1.67 GPa | 242 ksi | 50 mm/min; ASTM D638 |
| Flexural Strength | 70.6 MPa | 10200 psi | 2.8 mm/min; ASTM D638 |
| Flexural Modulus | 2.01 GPa | 292 ksi | 2.8 mm/min; ASTM D638 |
| Izod Impact, Notched | 1.47 J/cm @Thickness 6.35 mm, Temperature -30.0 °C |
2.76 ft-lb/in @Thickness 0.250 in, Temperature -22.0 °F |
ASTM D256 |
| 1.57 J/cm @Thickness 3.17 mm, Temperature -30.0 °C |
2.94 ft-lb/in @Thickness 0.125 in, Temperature -22.0 °F |
ASTM D256 | |
| 3.43 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
6.43 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
ASTM D256 | |
| 6.08 J/cm @Thickness 3.17 mm, Temperature 23.0 °C |
11.4 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
ASTM D256 | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C @Thickness 6.40 mm |
239 °F @Thickness 0.252 in |
ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 106 °C @Thickness 6.40 mm |
223 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 120 °C | 248 °F | B/50; ISO R306 |
| Optical Properties | Metric | English | Comments |
| Gloss | 35 % @Temperature 23.0 °C |
35 % @Temperature 73.4 °F |
50% RH, 60°; ASTM D2457 |