Availability
|
|
|||
|
Additive
|
|
|||
|
Features
|
|
|||
|
Appearance
|
|
|||
|
Forms
|
|
|||
|
Processing Method
|
|
| Physical |
Nominal Value
|
Unit
|
Test Method
|
|
Specific Gravity
|
1.15
|
g/cm³
|
ASTM D792 |
|
Molding Shrinkage
|
ASTM D955 | ||
|
Flow: 1.60 mm, Injection Molded
|
0.80
|
%
|
|
|
Flow: 3.20 mm, Injection Molded
|
1.1
|
%
|
|
|
Across Flow: 1.60 mm, Injection Molded
|
0.80
|
%
|
|
|
Across Flow: 3.20 mm, Injection Molded
|
1.1
|
%
|
| Mechanical |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Strength (Ultimate, Injection Molded)
|
89.2
|
MPa
|
ASTM D638 |
|
Tensile Elongation (Break, Injection Molded)
|
14
|
%
|
ASTM D638 |
|
Flexural Modulus (Injection Molded)
|
3430
|
MPa
|
ASTM D790 |
| Impact |
Nominal Value
|
Unit
|
Test Method
|
|
Unnotched Izod Impact
|
43
|
J/m
|
ASTM D256 |
| Thermal |
Nominal Value
|
Unit
|
Test Method
|
|
Deflection Temperature Under Load
|
ASTM D648 | ||
|
0.45 MPa, Unannealed
|
230
|
°C
|
|
|
1.8 MPa, Unannealed
|
70.0
|
°C
|
|
|
Melting Temperature
|
263
|
°C
|
DSC |
|
RTI Elec
|
UL 746 | ||
|
1.50 mm
|
130
|
°C
|
|
|
3.00 mm
|
130
|
°C
|
|
|
RTI Imp
|
UL 746 | ||
|
1.50 mm
|
75.0
|
°C
|
|
|
3.00 mm
|
75.0
|
°C
|
|
|
RTI Str
|
UL 746 | ||
|
1.50 mm
|
85.0
|
°C
|
|
|
3.00 mm
|
85.0
|
°C
|
| Flammability |
Nominal Value
|
|
Test Method
|
|
Flame Rating
|
UL 94, IEC 60695-11-10, -20 | ||
|
0.800 mm
|
V-0
|
|
|
|
1.50 mm
|
V-0
|
|
|
|
3.00 mm
|
V-0
|
|