vailability
|
|
|||
|
Features
|
|
|||
|
Uses
|
|
|||
|
UL File Number
|
|
|||
|
Processing Method
|
|
| Physical |
Nominal Value
|
Unit
|
Test Method
|
|
Specific Gravity
|
1.12
|
g/cm³
|
ASTM D792 |
|
Molding Shrinkage - Flow
|
1.2 to 1.8
|
%
|
ASTM D955 |
| Mechanical |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Strength
|
40.0
|
MPa
|
ASTM D638 |
|
Tensile Elongation (Break)
|
120
|
%
|
ASTM D638 |
|
Flexural Modulus
|
1500
|
MPa
|
ASTM D790 |
|
Flexural Strength
|
50.0
|
MPa
|
ASTM D790 |
| Impact |
Nominal Value
|
Unit
|
Test Method
|
|
Charpy Notched Impact Strength (3.20 mm)
|
850
|
J/m
|
ASTM D256 |
| Thermal |
Nominal Value
|
Unit
|
Test Method
|
|
Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm)
|
80.0
|
°C
|
ASTM D648 |
| Flammability |
Nominal Value
|
|
Test Method
|
|
Flame Rating
|
HB
|
|
UL 94 |
| Injection |
Nominal Value
|
Unit
|
|
|
Drying Temperature
|
100 to 120
|
°C
|
|
|
Drying Time
|
3.0 to 5.0
|
hr
|
|
|
Processing (Melt) Temp
|
220 to 290
|
°C
|
|
|
Mold Temperature
|
50.0 to 90.0
|
°C
|
|
|
Injection Pressure
|
30.0 to 110
|
MPa
|