TPU 58144 物性表：
个别产品成品图片
TPU 58144 物性表：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.18 g/cc | 1.18 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 62 - 68 | 62 - 68 | ASTM D2240 |
| Tensile Strength, Ultimate | 45.9 MPa | 6660 psi | ASTM D412; ASTM D638 |
| Tensile Strength, Yield | 24.1 MPa | 3500 psi | 100% elongation; ASTM D412; ASTM D638 |
| 38.7 MPa | 5610 psi | 300% elongation; ASTM D412; ASTM D638 | |
| Elongation at Break | 340 % | 340 % | ASTM D412; ASTM D638 |
| Flexural Modulus | 0.3097 GPa @Temperature 23.0 °C |
44.92 ksi @Temperature 73.4 °F |
ASTM D790 |
| Flexural Stiffness | 217.4 MPa @Temperature 23.0 °C |
31530 psi @Temperature 73.4 °F |
ASTM D747 |
| Tear Strength | 35.9 kN/m | 205 pli | Split; ASTM D470 |
| 170.9 kN/m | 975.2 pli | Die C; ASTM D624 | |
| Compression Set | 66 % @Temperature 23.0 °C, Time 79200 sec |
66 % @Temperature 73.4 °F, Time 22.0 hour |
ASTM D395 |
| 93 % @Temperature 70.0 °C, Time 79200 sec |
93 % @Temperature 158 °F, Time 22.0 hour |
ASTM D395 | |
| Tensile Set | 53 % | 53 % | 200% elongation; ASTM D412 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 102 °C | 216 °F | ASTM D1525 |
| Glass Transition Temp, Tg | -40.0 °C | -40.0 °F | DSC |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 199 °C | 390 °F | |
| Middle Barrel Temperature | 240 °C | 464 °F | |
| Front Barrel Temperature | 215 °C | 419 °F | |
| Nozzle Temperature | 218 °C | 424 °F | |
| Melt Temperature | 204 °C | 399 °F | |
| Mold Temperature | 10.0 - 22.0 °C | 50.0 - 71.6 °F | |
| Drying Temperature | 104 °C @Time 7200 sec |
219 °F @Time 2.00 hour |
|
| Injection Pressure | 68.9 - 138 MPa | 10000 - 20000 psi | |
| Back Pressure | 0.345 MPa | 50.0 psi | |
| Screw Speed | 20 - 50 rpm | 20 - 50 rpm |
|
应用介绍：
1．薄膜和片材（TPU具较好耐磨性、抗刺穿性、抗撕裂性、弹性、粘合性）（TPU薄膜应用在冬季服装、鞋类具有防寒、保暖、防水性能好等特性外还具有特别好的透气性）
2．管材（TPU具有高伸长率，良好耐水解和抗微生物性、耐油性、优异机械性能，如作消防水管内衬，输油管气动软管等）
3．鞋底，鞋邦等鞋材料（TPU具有突出耐磨性、抗刮性、耐刺穿性、抗纵向弯曲强度和低温冲击强度，其耐撕裂性和抗裂纹传播性是所有塑料中最好的。如作溜冰、滑雪靴、运动鞋、特种功能鞋等）
4．电线、电缆、光缆护套（TPU具良好耐磨性、耐环境、耐候性、耐腐蚀性、绝缘性、弹性和低温柔韧性等）
5．拉链片、高档塑料表带、表壳以及潜水表、礼品表等系列（TPU具有高弹、耐折、耐水性好手感舒适等）
6．机械制品和其它应用（如制造汽车部件、机械轴承、滚轮、输送带、橡塑筛网、工业胶管,垫圈,密封圈,游泳镜,冲浪板,表带,动物标牌,电器零部件,涂料,粘合剂,纤维等.)
上海松翰塑化科技有限公司供应产品，品质一流，TPV种类齐全。 公司理念你的要求就是我们的追求 。咨询人夏先生 电话：13751253137 QQ：205730283 我公司将给你最专业产品加工工艺指导及帮你解决加工工艺难题 欢迎你的咨询