特点：
1、综合性能较好，冲击强度较高，化学稳定性，电性能良好.
2、与372有机玻璃的熔接性良好，制成双色塑件，且可表面镀铬，喷漆处理.
3、有高抗冲、高耐热、阻燃、增强、透明等级别。
4、流动性比HIPS差一点，比PMMA、PC等好，柔韧性好。
5、用途：适于制作一般机械零件，减磨耐磨零件，传动零件和电讯零件.
6、同PVC（聚氯乙烯）一样在屈折处会出现白化现象。
典型应用范围:
汽车内外饰：仪表板，饰柱，仪表前盖，格栅，内外饰件 2.商务设备机壳和内置部件：笔记本/台式电脑，复印机，打印机，绘图仪，显示器 3.电信，移动电话外壳，附件以及智能卡（SIM卡）： 4.电器产品，电子产品外壳，电表罩和壳体，家用开关，插头和插座，电缆电线管道 5.家用电器，如洗衣机，吹风机，微波炉内外部件等。
物性表：
| General Information | ||||
| General | ||||
|
Material Status
|
|
|||
|
Availability
|
|
|||
|
Additive
|
|
|||
|
Features
|
|
|||
|
Appearance
|
|
|||
|
Processing Method
|
|
|||
| ASTM & ISO Properties 1 | |||
| Physical |
Nominal Value
|
Unit
|
Test Method
|
|
Specific Gravity
|
1.18
|
g/cm³
|
ASTM D792 |
|
Molding Shrinkage - Flow (3.18 mm)
|
0.50
|
%
|
ASTM D955 |
|
Water Absorption (24 hr)
|
0.10
|
%
|
ASTM D570 |
| Mechanical |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Strength (Break)
|
56.5
|
MPa
|
ASTM D638 |
|
Tensile Elongation (Break)
|
50
|
%
|
ASTM D638 |
|
Flexural Modulus
|
2690
|
MPa
|
ASTM D790 |
|
Flexural Strength
|
103
|
MPa
|
ASTM D790 |
| Impact |
Nominal Value
|
Unit
|
Test Method
|
|
Notched Izod Impact (23°C, 3.18 mm)
|
510
|
J/m
|
ASTM D256 |
|
Instrumented Dart Impact (23°C, Total Energy)
|
58.8
|
J
|
ASTM D3763 |
| Hardness |
Nominal Value
|
Unit
|
Test Method
|
|
Rockwell Hardness (R-Scale)
|
120
|
|
ASTM D785 |
| Thermal |
Nominal Value
|
Unit
|
Test Method
|
|
Deflection Temperature Under Load (0.45 MPa, Unannealed)
|
93.3 to 100
|
°C
|
ASTM D648 |
|
Deflection Temperature Under Load (1.8 MPa, Unannealed)
|
87.8 to 94.4
|
°C
|
ASTM D648 |
|
CLTE - Flow
|
7.2E-5
|
cm/cm/°C
|
ASTM D696 |
| Electrical |
Nominal Value
|
Unit
|
Test Method
|
|
Surface Resistivity
|
1.0E+15
|
ohms
|
ASTM D257 |
|
Volume Resistivity
|
1.0E+17
|
ohms·cm
|
ASTM D257 |
| Flammability |
Nominal Value
|
Unit
|
Test Method
|
|
Flame Rating (1.57 mm)
|
HB
|
|
UL 94 |