| Physical | Dry | Conditioned |
Unit
|
Test Method
|
|
Density
|
1.15
|
--
|
g/cm³
|
ISO 1183/A |
| Hardness | Dry | Conditioned |
Unit
|
Test Method
|
|
Shore Hardness (Shore D)
|
85
|
79
|
|
ISO 868 |
| Mechanical | Dry | Conditioned |
Unit
|
Test Method
|
|
Tensile Stress
|
ISO 527-2 | |||
|
Yield
|
85.0
|
55.0
|
MPa
|
|
|
Break
|
70.0
|
65.0
|
MPa
|
|
|
Tensile Strain (Break)
|
30
|
50
|
%
|
ISO 527-2 |
|
Flexural Modulus
|
2900
|
1300
|
MPa
|
ISO 178 |
| Impact | Dry | Conditioned |
Unit
|
Test Method
|
|
Charpy Notched Impact Strength
|
5.0
|
13
|
kJ/m²
|
ISO 179/1eA |
|
Charpy Unnotched Impact Strength
|
No Break
|
No Break
|
|
ISO 179/1eU |
|
Notched Izod Impact Strength
|
4.5
|
14
|
kJ/m²
|
ISO 180/1A |
| Thermal | Dry | Conditioned |
Unit
|
Test Method
|
|
Heat Deflection Temperature (1.8 MPa, Unannealed)
|
90.0
|
--
|
°C
|
ISO 75-2/Af |
|
Melting Temperature (DSC)
|
260
|
--
|
°C
|
ISO 3146 |
|
CLTE - Flow
|
0.000070
|
--
|
cm/cm/°C
|
ASTM E831 |
| Electrical | Dry | Conditioned |
Unit
|
Test Method
|
|
Surface Resistivity
|
1.0E+15
|
1.0E+14
|
ohm
|
IEC 60093 |
|
Volume Resistivity
|
1.0E+15
|
1.0E+14
|
ohm·cm
|
IEC 60093 |
|
Comparative Tracking Index (Solution A)
|
600
|
--
|
V
|
IEC 60112 |