生产工艺分间歇法和连续法两种。连续法适合大规模生产，世界上生产尼龙66主要采用连续法。间歇法仅在两种情况下采用：一是生产特殊或试验品级;二是在生产能力为4 500t A 以下的小装置中。
物性表：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.50 g/cc | 0.0542 lb/in³ | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 193.1 MPa | 28010 psi | ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | ASTM D638 |
| Flexural Modulus | 10.34 GPa | 1500 ksi | ASTM D790 |
| Izod Impact, Notched | 1.07 J/cm @Thickness 3.17 mm |
2.00 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 254 °C | 489 °F | ASTM D789 |
| Deflection Temperature at 1.8 MPa (264 psi) | 251 °C | 484 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 254 °C | 490 °F | |
| Middle Barrel Temperature | 268 °C | 515 °F | |
| Front Barrel Temperature | 285 °C | 545 °F | |
| Nozzle Temperature | 266 - 282 °C | 510 - 540 °F | |
| Melt Temperature | 271 - 293 °C | 520 - 560 °F | |
| Mold Temperature | 26.7 - 93.3 °C | 80.0 - 200 °F | |
| Drying Temperature | 71.1 °C | 160 °F | |
| Dry Time | 4 hour | 4 hour | |
| Injection Pressure | 68.9 MPa | 10000 psi | |
| Back Pressure | 0.0689 - 0.689 MPa | 10.0 - 100 psi | |
| Screw Speed | 30 - 60 rpm | 30 - 60 rpm | |
防静电PA，导电PA，加纤防火PA，防火PA，抗紫外线耐候PA，高温挤出级PA。
颗粒图：电子电器：连接器、卷线轴、计时器、护盖断路器、开关壳座
汽车： 散热风扇、门把、油箱盖、进气隔栅、水箱护盖、灯座
工业零件：椅座、自行车输框、溜冰鞋底座、纺织梭、踏板、滑输