颗粒样图：
物性表：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.45 g/cc | 0.0524 lb/in³ | ISO 1183 & ASTM D792 |
| Linear Mold Shrinkage | 0.0010 - 0.0020 cm/cm | 0.0010 - 0.0020 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0020 - 0.0030 cm/cm | 0.0020 - 0.0030 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 215 MPa | 31200 psi | 5 mm/min; ISO 527-2/1A |
| 253 MPa | 36700 psi | ASTM D638 | |
| 270 MPa @Temperature -40.0 °C |
39100 psi @Temperature -40.0 °F |
ASTM D638 | |
| Tensile Strength, Ultimate | 134 MPa @Temperature 121 °C |
19400 psi @Temperature 250 °F |
ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | 5 mm/min; ISO 527-2/1A |
| 2.3 % | 2.3 % | ASTM D638 | |
| 2.2 % @Temperature -40.0 °C |
2.2 % @Temperature -40.0 °F |
ASTM D638 | |
| 2.5 % @Temperature 121 °C |
2.5 % @Temperature 250 °F |
ASTM D638 | |
| Tensile Modulus | 13.3 GPa | 1930 ksi | 1 mm/min; ISO 527-2/1A |
| 14.2 GPa | 2060 ksi | ASTM D638 | |
| 7.31 GPa @Temperature 121 °C |
1060 ksi @Temperature 250 °F |
ASTM D638 | |
| 14.5 GPa @Temperature -40.0 °C |
2100 ksi @Temperature -40.0 °F |
ASTM D638 | |
| Flexural Strength | 355 MPa | 51500 psi | ISO 178 |
| 359 MPa | 52000 psi | ASTM D790 | |
| 181 MPa @Temperature 121 °C |
26300 psi @Temperature 250 °F |
ASTM D790 | |
| 388 MPa @Temperature -40.0 °C |
56300 psi @Temperature -40.0 °F |
ASTM D790 | |
| Flexural Modulus | 11.8 GPa | 1710 ksi | ISO 178 |
| 12.3 GPa | 1780 ksi | ASTM D790 | |
| 6.48 GPa @Temperature 121 °C |
940 ksi @Temperature 250 °F |
ASTM D790 | |
| 12.45 GPa @Temperature -40.0 °C |
1805 ksi @Temperature -40.0 °F |
ASTM D790 | |
| Izod Impact, Notched | 3.68 J/cm | 6.90 ft-lb/in | ASTM D256 |
| 4.64 J/cm | 8.70 ft-lb/in | at 250°F; ASTM D256 | |
| 3.95 J/cm @Temperature -40.0 °C |
7.40 ft-lb/in @Temperature -40.0 °F |
ASTM D256 | |
| Charpy Impact, Notched | 3.50 J/cm² | 16.7 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 255 °C | 491 °F | ISO 75-1, -2 & ASTM D648 |
应用：广泛用于制造机械、汽车、化学与电气装置的零件，如齿轮、滚子、滑轮、辊轴、泵体中叶轮、风扇叶片、高压密封围、阀座、垫片、衬套、各种把手、支撑架、电线包内层等。