颗粒样图：
应用：广泛用于制造机械、汽车、化学与电气装置的零件，如齿轮、滚子、滑轮、辊轴、泵体中叶轮、风扇叶片、高压密封围、阀座、垫片、衬套、各种把手、支撑架、电线包内层等。
上海松翰塑化科技有限公司，供应原料，品质真实,物实价廉。
PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。
欢迎各位客户前来咨询：
联系人： 夏先生
手 机：13501802636
QQ ：205730283
邮 箱 ：205730283@qq.com
物性表：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.40 g/cc | 1.40 g/cc | ASTM D792 |
| Water Absorption | 0.70 % | 0.70 % | ASTM D570 |
| Maximum Moisture Content | 0.090 | 0.090 | Injection Molding |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.011 cm/cm @Thickness 3.20 mm |
0.0050 - 0.011 in/in @Thickness 0.126 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 122 | 122 | ASTM D785 |
| Tensile Strength, Yield | 186 MPa @Thickness 3.20 mm |
27000 psi @Thickness 0.126 in |
5mm/min; ASTM D638 |
| Elongation at Break | 2.0 % @Thickness 3.20 mm |
2.0 % @Thickness 0.126 in |
5mm/min; ASTM D638 |
| Flexural Yield Strength | 186 MPa @Thickness 3.20 mm |
27000 psi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
| Flexural Modulus | 5.88 GPa @Thickness 3.20 mm |
853 ksi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
| Izod Impact, Notched | 0.490 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
0.918 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | ASTM D257 |
| Dielectric Strength | 21.0 kV/mm @Thickness 1.00 mm |
533 kV/in @Thickness 0.0394 in |
ASTM D149 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 40.0 µm/m-°C | 22.2 µin/in-°F | ASTM D696 |
| Melting Point | 260 °C | 500 °F | ASTM D3418 |
| Deflection Temperature at 1.8 MPa (264 psi) | 235 °C @Thickness 6.40 mm |
455 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 270 - 285 °C | 518 - 545 °F | Injection Molding |
| Middle Barrel Temperature | 275 - 290 °C | 527 - 554 °F | Injection Molding |
| Front Barrel Temperature | >= 280 °C | >= 536 °F | Injection Molding |
| Nozzle Temperature | 280 - 295 °C | 536 - 563 °F | Injection Molding |
| Melt Temperature | 270 - 295 °C | 518 - 563 °F | Injection Molding |
| Mold Temperature | 80.0 - 110 °C | 176 - 230 °F | Injection Molding |
| Drying Temperature | 80.0 - 100 °C | 176 - 212 °F | Injection Molding |
| Dry Time | 4.00 - 5.00 hour | 4.00 - 5.00 hour | Injection Molding |
| Back Pressure | 29.4 - 58.8 MPa | 4260 - 8530 psi | Injection Molding |
| Screw Speed | 30 - 60 rpm | 30 - 60 rpm | Injection Molding |