颗粒：
广泛用于制造机械、汽车、化学与电气装置的零件，如齿轮、滚子、滑轮、辊轴、泵体中叶轮、风扇叶片、高压密封围、阀座、垫片、衬套、各种把手、支撑架、电线包层等。亦可制成薄膜用作包装材料。此外，还可用于制作医疗器械、体育用品、日用品等。
上海松翰塑化科技有限公司，供应原料，品质真实,物实价廉。
PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。
欢迎各位客户前来咨询：
联系人： 夏先生
手 机：13501802636
QQ ：205730283
邮 箱 ：205730283@qq.com
物性表:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.45 g/cc | 1.45 g/cc | ASTM D792 |
| Water Absorption | 0.70 % @Temperature 23.0 °C, Time 86400 sec |
0.70 % @Temperature 73.4 °F, Time 24.0 hour |
ASTM D570 |
| Maximum Moisture Content | 0.090 | 0.090 | Injection Molding |
| Linear Mold Shrinkage, Flow | 0.0070 - 0.012 cm/cm @Thickness 3.20 mm |
0.0070 - 0.012 in/in @Thickness 0.126 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength, Yield | 95.6 MPa @Thickness 3.20 mm |
13900 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Elongation at Break | 5.0 % @Thickness 3.20 mm |
5.0 % @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Flexural Yield Strength | 142 MPa @Thickness 6.40 mm |
20600 psi @Thickness 0.252 in |
2.8mm/min; ASTM D790 |
| Flexural Modulus | 4.90 GPa @Thickness 6.40 mm |
711 ksi @Thickness 0.252 in |
2.8mm/min; ASTM D790 |
| Izod Impact, Notched | 0.392 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
0.735 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Arc Resistance | 0.00 - 60 sec | 0.00 - 60 sec | ASTM D495 |
| Comparative Tracking Index | 250 - 400 V | 250 - 400 V | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 70.0 µm/m-°C | 38.9 µin/in-°F | ASTM D696 |
| Melting Point | 260 °C | 500 °F | ASTM D3418 |
| Deflection Temperature at 1.8 MPa (264 psi) | 232 °C @Thickness 6.40 mm |
450 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| UL RTI, Electrical | 65.0 °C @Thickness 0.750 - 0.820 mm |
149 °F @Thickness 0.0295 - 0.0323 in |
|
| UL RTI, Mechanical with Impact | 65.0 °C @Thickness 0.750 - 0.820 mm |
149 °F @Thickness 0.0295 - 0.0323 in |
|
| UL RTI, Mechanical without Impact | 65.0 °C @Thickness 0.750 - 0.820 mm |
149 °F @Thickness 0.0295 - 0.0323 in |
|
| Flammability, UL94 | V-0 @Thickness >=0.800 mm |
V-0 @Thickness >=0.0315 in |
|
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 265 - 275 °C | 509 - 527 °F | Injection Molding |
| Middle Barrel Temperature | 270 - 280 °C | 518 - 536 °F | Injection Molding |
| Front Barrel Temperature | 270 - 285 °C | 518 - 545 °F | Injection Molding |
| Nozzle Temperature | 270 - 280 °C | 518 - 536 °F | Injection Molding |
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | Injection Molding |
| Mold Temperature | 80.0 - 110 °C | 176 - 230 °F | Injection Molding |
| Drying Temperature | 80.0 - 100 °C | 176 - 212 °F | Injection Molding |
| Dry Time | 4.00 - 5.00 hour | 4.00 - 5.00 hour | Injection Molding |
| Back Pressure | 29.4 - 58.8 MPa | 4260 - 8530 psi | Injection Molding |
| Screw Speed | 30 - 60 rpm | 30 - 60 rpm | Injection Molding |