颗粒图： 
用途：
广泛应用于机械、仪器仪表、汽车部件、电子电气、铁路、家电、通讯、纺机、体育休闲用品、油管、油箱及一些精密工程制品。
电子电器：连接器、卷线轴、计时器、护盖断路器、开关壳座。
汽车： 散热风扇、门把、油箱盖、进气隔栅、水箱护盖、灯座。
工业零件：椅座、自行车输框、溜冰鞋底座、纺织梭、踏板、滑输。
上海松翰塑化科技有限公司，供应原料，品质真实,物实价廉。
PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。
欢迎各位客户前来咨询：
联系人： 夏先生
手 机：13501802636
QQ ：205730283
邮 箱 ：205730283@qq.com
物性表:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in³ | ISO 1183-A |
| Water Absorption | 0.75 % | 0.75 % | (Beginning Dry) 24 hours in water 23°C. ISO 62 |
| Linear Mold Shrinkage | 0.0045 cm/cm | 0.0045 in/in | RHODIA-EP |
| Linear Mold Shrinkage, Transverse | 0.0075 cm/cm | 0.0075 in/in | RHODIA-EP |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 150 MPa | 21800 psi | ISO 527 |
| Tensile Strength, Yield | 150 MPa | 21800 psi | ISO 527 |
| Elongation at Break | 4.0 % | 4.0 % | ISO 527 |
| Tensile Modulus | 8.70 GPa | 1260 ksi | ISO 527 |
| Flexural Yield Strength | 195 MPa | 28300 psi | ISO 178 |
| Flexural Modulus | 6.80 GPa | 986 ksi | ISO 178 |
| Izod Impact Resistance | 1.80 J/cm² | 8.57 ft-lb/in² | ISO 180 |
| Charpy Impact Unnotched | 10.0 J/cm² | 47.6 ft-lb/in² | ISO 179/1EA-1993 |
| Charpy Impact, Notched | 1.85 J/cm² | 8.80 ft-lb/in² | ISO 179/1EA-1993 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | IEC 93 |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 93 |
| Dielectric Constant | 4.0 @Frequency 1e+6 Hz |
4.0 @Frequency 1e+6 Hz |
IEC 250 |
| Dielectric Strength | 29.0 kV/mm | 737 kV/in | IEC 243-1 |
| Dissipation Factor | 0.11 @Frequency 1e+6 Hz |
0.11 @Frequency 1e+6 Hz |
IEC 250 |
| Comparative Tracking Index | 450 V | 450 V | IEC 112 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 263 °C | 505 °F | ISO 3146-C |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 260 - 270 °C | 500 - 518 °F | |
| Middle Barrel Temperature | 270 - 280 °C | 518 - 536 °F | |
| Front Barrel Temperature | 280 - 290 °C | 536 - 554 °F | |