具自熄性、PA66 2710IR_产品资讯

PA66 2710IR 塑胶原料为半透明或不透明乳白包或带黄色颗粒状结晶形聚合物，具有可塑性。密度（g/cm3） 1．10-1．14；拉伸强度(MPa) 60. 0-80．0；洛氏硬度118；熔点252℃；脆化温度-30℃；热分解温度大于350℃；连续耐热80-120℃；冲击强度（kJ/m2） 60-100；静弯曲强度(MPa) 1 00-120；马丁耐热(℃) 50-60；弯曲弹性模量 (MPa) 2000～3000；体积电阻率（Ωcm） 1.83×1015；平衡吸水率2．5%；介电常数 1．63。

颗粒样图：

物性表:

Physical Properties	Metric	English	Comments

Density	1.10 g/cc	0.0397 lb/in³	ISO 1183
Water Absorption	1.1 % @Temperature 23.0 °C, Time 86400 sec	1.1 % @Temperature 73.4 °F, Time 24.0 hour	ISO 62
Linear Mold Shrinkage, Flow	0.019 cm/cm	0.019 in/in
Linear Mold Shrinkage, Transverse	0.019 cm/cm	0.019 in/in

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	65.0 MPa	9430 psi	ISO 527 type 1 A
Elongation at Break	25 %	25 %	ISO 527 Type 1A
Flexural Strength	90.0 MPa	13100 psi	ISO 178
Flexural Modulus	2.10 GPa	305 ksi	ISO 178
Izod Impact, Notched (ISO)	22.0 kJ/m²	10.5 ft-lb/in²	ISO 180/1A
Charpy Impact Unnotched	NB	NB	ISO 179/1eU
Charpy Impact, Notched	1.50 J/cm²	7.14 ft-lb/in²	ISO 179/1eA

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+15 ohm-cm	1.00e+15 ohm-cm	IEC 60093
Surface Resistance	1.00e+15 ohm	1.00e+15 ohm	IEC 60093
Dielectric Constant	3.2	3.2	IEC60250
Dielectric Strength	30.0 kV/mm	762 kV/in	IEC 60243
Dissipation Factor	0.020	0.020	IEC 60250
Comparative Tracking Index	475 V	475 V	Solution B; IEC 60112
	550 V	550 V	Solution A; IEC 60112

Thermal Properties	Metric	English	Comments
CTE, linear	12.6 µm/m-°C @Temperature 23.0 - 85.0 °C	7.00 µin/in-°F @Temperature 73.4 - 185 °F	ASTM D696
Melting Point	262 °C	504 °F	ISO 11357
Deflection Temperature at 0.46 MPa (66 psi)	92.0 °C	198 °F	ISO 75/Af
Deflection Temperature at 1.8 MPa (264 psi)	92.0 °C	198 °F	ISO 75/Af
Flammability, UL94	HB @Thickness 3.20 mm	HB @Thickness 0.126 in	ISO 1210
Oxygen Index	21 %	21 %	ISO 4589

Processing Properties	Metric	English	Comments
Feed Temperature	265 - 270 °C	509 - 518 °F
Mold Temperature	70.0 - 100 °C	158 - 212 °F
Drying Temperature	80.0 °C	176 °F
Moisture Content	<= 0.20 %	<= 0.20 %

Descriptive Properties
Compression Zone	270-280°C
Mixing Zone	280-290°C

应用：广泛用于制造机械、汽车、化学与电气装置的零件，如齿轮、滚子、滑轮、辊轴、泵体中叶轮、风扇叶片、高压密封围、阀座、垫片、衬套、各种把手、支撑架、电线包内层等。