 PA66 A 216 NATURAL PA66塑胶原料为半透明或不透明乳白包或带黄色颗粒状结晶形聚合物，具有可塑性。密度（g/cm3） 1．10-1．14；拉伸强度(MPa) 60. 0-80．0；洛氏硬度118；熔点252℃；脆化温度-30℃；热分解温度大于350℃；连续耐热80-120℃；冲击强度（kJ/m2） 60-100；静弯曲强度(MPa) 1 00-120；马丁耐热(℃) 50-60；弯曲弹性模量 (MPa) 2000～3000；体积电阻率（Ωcm） 1.83×1015；平衡吸水率2．5%；介电常数 1．63。

Physical Properties	Metric	English	Comments
Density	1.14 g/cc	0.0412 lb/in³	ISO 1183/A
Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	65.0 MPa	9430 psi	ISO 527 Type 1A
Tensile Strength, Yield	60.0 MPa	8700 psi	ISO 527 type 1 A
Elongation at Break	300 %	300 %	ISO 527 Type 1A
Elongation at Yield	30 %	30 %	ISO 527 type 1 A
Tensile Modulus	1.50 GPa	218 ksi	ISO 527 Type 1A
Flexural Strength	50.0 MPa	7250 psi	ISO 178
Flexural Modulus	1.30 GPa	189 ksi	ISO 178
Izod Impact, Notched (ISO)	12.0 kJ/m²	5.71 ft-lb/in²	ISO 180/1A
Charpy Impact Unnotched	NB	NB	ISO 179/1eU
Charpy Impact, Notched	1.40 J/cm²	6.66 ft-lb/in²	ISO 179/1eA
Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+13 ohm-cm	1.00e+13 ohm-cm	IEC 60093
Surface Resistance	1.00e+12 ohm	1.00e+12 ohm	IEC 60093
Dielectric Constant	3.2	3.2	IEC 60250
Dielectric Strength	26.0 kV/mm	660 kV/in	IEC 60243
Dissipation Factor	0.080	0.080	IEC 60250
Comparative Tracking Index	575 V	575 V	Solution A; IEC 60112
Processing Properties	Metric	English	Comments
Moisture Content	<= 0.20 %	<= 0.20 %