| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ISO 1183/A | ||
| Water Absorption | 1.2 % @Temperature 23.0 °C, Time 86400 sec |
1.2 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62 | ||
| Linear Mold Shrinkage | 0.010 cm/cm | 0.010 in/in | Isotropy | ||
| Linear Mold Shrinkage, Flow | 0.020 cm/cm | 0.020 in/in | |||
| Linear Mold Shrinkage, Transverse | 0.020 cm/cm | 0.020 in/in | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 60.0 MPa | 8700 psi | ISO 527 Type 1A | ||
| Tensile Strength, Yield | 85.0 MPa | 12300 psi | ISO 527 type 1 A | ||
| Elongation at Yield | 7.0 % | 7.0 % | ISO 527 type 1 A | ||
| Tensile Modulus | 3.20 GPa | 464 ksi | ISO 527 Type 1A | ||
| Flexural Modulus | 2.90 GPa | 421 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 4.50 kJ/m² | 2.14 ft-lb/in² | ISO 180/1A | ||
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU | ||
| Charpy Impact, Notched | 0.450 J/cm² | 2.14 ft-lb/in² | ISO 179/1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 | ||
| Dielectric Constant | 2.9 | 2.9 | IEC 60250 | ||
| Dielectric Strength | 27.0 kV/mm | 686 kV/in | IEC 60243 | ||
| Dissipation Factor | 0.030 | 0.030 | IEC 60250 | ||
| Comparative Tracking Index | 375 V | 375 V | Solution B; IEC 60112 | ||
| 475 V | 475 V | Solution A; IEC 60112 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 12.6 µm/m-°C @Temperature 23.0 - 85.0 °C |
7.00 µin/in-°F @Temperature 73.4 - 185 °F |
ISO 11359 | ||
| Melting Point | 263 °C | 505 °F | ISO 11357 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | ISO 75/Af | ||
| Flammability, UL94 | V-2 @Thickness 0.380 mm |
V-2 @Thickness 0.0150 in |
ISO 1210 | ||
| V-2 @Thickness 0.800 mm |
V-2 @Thickness 0.0315 in |
ISO 1210 | |||
| V-2 @Thickness 1.60 mm |
V-2 @Thickness 0.0630 in |
ISO 1210 | |||
| Oxygen Index | 26 % | 26 % | ISO 4589 | ||
| Glow Wire Test | 650 °C @Thickness 1.60 mm |
1200 °F @Thickness 0.0630 in |
Ignition Temperature; ISO 60695-2-13 | ||
| 850 °C @Thickness 1.60 mm |
1560 °F @Thickness 0.0630 in |
ISO 60695-2-12 | |||
| Processing Properties | Metric | English | Comments | ||
| Feed Temperature | 270 - 275 °C | 518 - 527 °F | |||
| Front Barrel Temperature | 285 - 290 °C | 545 - 554 °F | |||
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |||
| Drying Temperature | 80.0 °C | 176 °F | |||
| Moisture Content | <= 0.20 % | <= 0.20 % | |||
| De |
|||||
| Mixing Zone | 280-285°C | ||||
广泛应用于机械、仪器仪表、汽车部件、电子电气、铁路、家电、通讯、纺机、体育休闲用品、油管、油箱及一些精密工程制品。
电子电器：连接器、卷线轴、计时器、护盖断路器、开关壳座。
汽车： 散热风扇、门把、油箱盖、进气隔栅、水箱护盖、灯座。
工业零件：椅座、自行车输框、溜冰鞋底座、纺织梭、踏板、滑输。
上海松翰塑化科技有限公司，供应原料，品质真实,物实价廉。
PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。
欢迎各位客户前来咨询：
联系人： 夏先生
手 机：13501802636
QQ ：205730283
邮 箱 ：205730283@qq.com