PA66 246M 冲击级, EH0、

PA66 246M 有可塑性。PA66 246M 密度1.15g/cm3。熔点252℃。脆化温度-30℃。PA66 246M 热分解温度大于350℃。 连续耐热80-120℃,平衡吸水率2.5%。能耐酸、碱、大多数无机盐水溶液、卤代烷、烃类、酯类、酮类等腐蚀。
 PA66 246M  聚酰胺俗称尼龙(Nylon),英文名称Polyamide(简称PA),是分子主链上含有重复酰胺基团—[NHCO]—的热塑性树脂总称。包括脂肪族PA,脂肪—芳香族PA和芳香族PA。其中,脂肪族PA品种多,产量大,应用广泛,其命名由合成单体具体的碳原子数而定。
颗粒图:H颗粒07   
物性表:
用途:
 
Physical Properties Metric English Comments
Density  1.08 g/cc 0.0390 lb/in³ ISO 1183-A
Water Absorption  1.05 % 1.05 % 24 hours in water at 23°C; ISO 62.
Linear Mold Shrinkage  0.019 cm/cm 0.019 in/in RHODIA-EP
Linear Mold Shrinkage, Transverse  0.019 cm/cm 0.019 in/in RHODIA-EP
 
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate  44.0 MPa 6380 psi ISO 527
Tensile Strength, Yield  47.0 MPa 6820 psi ISO 527
Elongation at Break  65 % 65 % ISO 527
Elongation at Yield  20 % 20 % ISO 527
Tensile Modulus  1.90 GPa 276 ksi ISO 527
Flexural Yield Strength  70.0 MPa 10200 psi ISO 178
Flexural Modulus  1.80 GPa 261 ksi ISO 178
Izod Impact, Notched (ISO)  22.0 kJ/m² 10.5 ft-lb/in² Low Temp; ISO 180
Izod Impact Resistance  6.00 J/cm² 28.6 ft-lb/in² ISO 180
Charpy Impact Unnotched  NB NB ISO 179/EU-1993
Charpy Impact, Notched  1.60 J/cm² 7.61 ft-lb/in² ISO 179/1EA-1993
  5.50 J/cm² 26.2 ft-lb/in² ISO 179/1EA-1993
 
Electrical Properties Metric English Comments
Electrical Resistivity  1.00e+15 ohm-cm 1.00e+15 ohm-cm IEC 93
Surface Resistance  1.00e+14 ohm 1.00e+14 ohm IEC 93
Dielectric Constant  3.2
@Frequency 1e+6 Hz
3.2
@Frequency 1e+6 Hz
IEC 250
Dielectric Strength  30.0 kV/mm 762 kV/in IEC 243-1
Dissipation Factor  0.020
@Frequency 1e+6 Hz
0.020
@Frequency 1e+6 Hz
IEC 250
Comparative Tracking Index  575 V 575 V IEC 112
 
Thermal Properties Metric English Comments
CTE, linear  70.0 µm/m-°C
@Temperature 23.0 - 85.0 °C
38.9 µin/in-°F
@Temperature 73.4 - 185 °F
ASTM E831
Melting Point  263 °C 505 °F ISO 3146-C
Deflection Temperature at 1.8 MPa (264 psi)  65.0 °C 149 °F ISO 75-2
Flammability, UL94  HB
@Thickness 1.60 mm
HB
@Thickness 0.0630 in
ISO 1210/UL 94
Oxygen Index  24.5 % 24.5 % ISO 4589
 
Processing Properties Metric English Comments
Rear Barrel Temperature  250 - 270 °C 482 - 518 °F  
Middle Barrel Temperature  260 - 280 °C 500 - 536 °F  
Front Barrel Temperature  270 - 290 °C 518 - 554 °F  
Melt Temperature  270 - 290 °C 518 - 554 °F  
Mold Temperature  60.0 - 90.0 °C 140 - 194 °F Surface
Drying Temperature  80.0 °C 176 °F Dehumidifying Dryer
Dry Time  3 - 4 hour 3 - 4 hour  
Moisture Content  <= 0.20 % <= 0.20 %  
Back Pressure  0.345 - 0.689 MPa 50.0 - 100 psi  
Fill Speed  300 - 600 mm/sec 11.8 - 23.6 in/sec Peripheral Screw Speed
 
Descriptive Properties
Injection Speed (cm3/sec) 80 - 150 cm3/sec
广泛应用于机械、仪器仪表、汽车部件、电子电气、铁路、家电、通讯、纺机、体育休闲用品、油管、油箱及一些精密工程制品。
电子电器:连接器、卷线轴、计时器、护盖断路器、开关壳座。
汽车: 散热风扇、门把、油箱盖、进气隔栅、水箱护盖、灯座。
工业零件:椅座、自行车输框、溜冰鞋底座、纺织梭、踏板、滑输。
 
上海松翰塑化科技有限公司,供应原料,品质真实,物实价廉。
PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。
欢迎各位客户前来咨询:
联系人: 夏先生  
手  机:13501802636   
QQ    :205730283  
邮 箱 :205730283@qq.com 
 
 

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/news/

本文链接: http://www.su-jiao.com/news/show-26430.html

免责声明: 本文 PA66 246M 冲击级, EH0、 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4