| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in³ | ASTM D792 | ||
| Linear Mold Shrinkage, Flow | 0.0070 - 0.010 cm/cm | 0.0070 - 0.010 in/in | |||
| Linear Mold Shrinkage, Transverse | 0.0090 - 0.012 cm/cm | 0.0090 - 0.012 in/in | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 140 MPa | 20300 psi | ASTM D638 | ||
| Elongation at Break | 4.0 % | 4.0 % | ASTM D638 | ||
| Flexural Strength | 200 MPa | 29000 psi | ASTM D790 | ||
| Flexural Modulus | 7.50 GPa | 1090 ksi | ASTM D790 | ||
| Izod Impact, Notched | 1.80 J/cm | 3.37 ft-lb/in | ASTM D265 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 262 °C | 504 °F | ISO 11357 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | ASTM D648 | ||
| Flammability, UL94 | HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
ISO 1210 | ||
| Processing Properties | Metric | English | Comments | ||
| Feed Temperature | 260 - 265 °C | 500 - 509 °F | |||
| Front Barrel Temperature | 275 - 285 °C | 527 - 545 °F | |||
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | |||
| Drying Temperature | 80.0 - 100 °C | 176 - 212 °F | |||
| Moisture Content | <= 0.20 % | <= 0.20 % | |||
| De |
|||||
| Compression Zone | 265-275°C | ||||
广泛用于制造机械、汽车、化学与电气装置的零件，如齿轮、滚子、滑轮、辊轴、泵体中叶轮、风扇叶片、高压密封围、阀座、垫片、衬套、各种把手、支撑架、电线包层等。亦可制成薄膜用作包装材料。此外，还可用于制作医疗器械、体育用品、日用品等。
上海松翰塑化科技有限公司，供应原料，品质真实,物实价廉。