颗粒： 
、
、
、 、物性表:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in³ | |
| Water Absorption | 2.6 % | 2.6 % | |
| Moisture Absorption at Equilibrium | 1.0 % | 1.0 % | Humidity Absorption |
| Melt Flow | 5.0 g/10 min @Load 2.16 kg, Temperature 235 °C |
5.0 g/10 min @Load 4.76 lb, Temperature 455 °F |
|
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 110 MPa | 16000 psi | 5 mm/min |
| Elongation at Break | 3.6 % | 3.6 % | 5 mm/min |
| Tensile Modulus | 4.95 GPa | 718 ksi | 1 mm/min |
| Charpy Impact, Notched | 1.05 J/cm² | 5.00 ft-lb/in² | |
| 0.840 J/cm² @Temperature -30.0 °C |
4.00 ft-lb/in² @Temperature -22.0 °F |
||
| Tensile Creep Modulus, 1 hour | 3800 MPa | 551000 psi | |
| Tensile Creep Modulus, 1000 hours | 2680 MPa | 389000 psi | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | |
| Dielectric Constant | 2.6 @Frequency 100 Hz |
2.6 @Frequency 100 Hz |
|
| 3.3 @Frequency 1e+6 Hz |
3.3 @Frequency 1e+6 Hz |
||
| Dielectric Strength | 35.0 kV/mm | 889 kV/in | |
| Dissipation Factor | 0.024 @Frequency 1e+6 Hz |
0.024 @Frequency 1e+6 Hz |
|
| 0.063 @Frequency 100 Hz |
0.063 @Frequency 100 Hz |
||
| Comparative Tracking Index | 600 V | 600 V | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 220 °C | 428 °F | 10°C/min |
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
||
广泛用于制造机械、汽车、化学与电气装置的零件，如齿轮、滚子、滑轮、辊轴、泵体中叶轮、风扇叶片、高压密封围、阀座、垫片、衬套、各种把手、支撑架、电线包层等。亦可制成薄膜用作包装材料。此外，还可用于制作医疗器械、体育用品、日用品等。