PA6 BFR460A 阻燃,注塑成型、

PA6 BFR460A 具有可塑性。密度1.15g/cm3。熔点252℃。PA6 BFR460A 脆化温度-30℃。热分解温度大于350℃。PA6 BFR460A 连续耐热80-120℃,平衡吸水率2.5%。能耐酸、碱、大多数无机盐水溶液、卤代烷、烃类、酯类、酮类等腐蚀。
 PA6 BFR460A  性状为半透明或不透明乳白色结晶形聚合物,具有可塑性。密度1.15g/cm3。熔点252℃。脆化温度-30℃。热分解温度大于350℃。 连续耐热80-120℃,平衡吸水率2.5%。能耐酸、碱、大多数无机盐水溶液、卤代烷、烃类、酯类、酮类等腐蚀,但易溶于苯酚、甲酸等极性溶剂。具有优良的耐磨性、自润滑性,机械强度较高。但吸水性较大,因而尺寸稳定性较差。
颗粒:images (17)  、
 
物性表:
 
Physical Properties Metric English Comments
Density  1.54 g/cc 0.0556 lb/in³ ISO 1183
Water Absorption at Saturation  5.0 %
@Temperature 23.0 °C
5.0 %
@Temperature 73.4 °F
ISO 62
Linear Mold Shrinkage, Flow  0.0020 - 0.0040 cm/cm 0.0020 - 0.0040 in/in on Tensile Bar; E2P method
 
Mechanical Properties Metric English Comments
Tensile Strength at Break  140 MPa 20300 psi 5 mm/min; ISO 527
Elongation at Break  3.0 % 3.0 % 5 mm/min; ISO 527
Tensile Modulus  8.80 GPa 1280 ksi 1 mm/min; ISO 527
Izod Impact, Notched (ISO)    6.00 kJ/m²
@Temperature -40.0 °C
2.86 ft-lb/in²
@Temperature -40.0 °F
80x10x4; ISO 180/1A
  7.00 kJ/m²
@Temperature -20.0 °C
3.33 ft-lb/in²
@Temperature -4.00 °F
80x10x4; ISO 180/1A
  9.00 kJ/m²
@Temperature 23.0 °C
4.28 ft-lb/in²
@Temperature 73.4 °F
80x10x4; ISO 180/1A
 
Electrical Properties Metric English Comments
Comparative Tracking Index  250 V 250 V IEC 60112
 
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow  17.0 µm/m-°C
@Temperature 23.0 - 60.0 °C
9.44 µin/in-°F
@Temperature 73.4 - 140 °F
ISO 11359-2
CTE, linear, Transverse to Flow  105 µm/m-°C
@Temperature 23.0 - 60.0 °C
58.3 µin/in-°F
@Temperature 73.4 - 140 °F
ISO 11359-2
Hot Ball Pressure Test  123 - 127 °C 253 - 261 °F IEC 60695-10-2
Deflection Temperature at 0.46 MPa (66 psi)  210 °C 410 °F Edgew 120x10x4, sp=100 mm; ISO 75/Be
Deflection Temperature at 1.8 MPa (264 psi)  195 °C 383 °F Edgew 120x10x4, sp=100 mm; ISO 75/Ae
UL RTI, Electrical  65.0 °C 149 °F  
UL RTI, Mechanical with Impact  65.0 °C 149 °F  
UL RTI, Mechanical without Impact  65.0 °C 149 °F  
Flammability, UL94  V-0
@Thickness 1.50 mm
V-0
@Thickness 0.0591 in
 
Glow Wire Test  960 °C
@Thickness 2.00 mm
1760 °F
@Thickness 0.0787 in
IEC 60695-2-12
 
Processing Properties Metric English Comments
Zone 1  240 - 250 °C 464 - 482 °F  
Zone 2  250 - 260 °C 482 - 500 °F  
Zone 3  250 - 270 °C 482 - 518 °F  
Melt Temperature  250 - 270 °C 482 - 518 °F  
Mold Temperature  50.0 - 90.0 °C 122 - 194 °F  
Drying Temperature  80.0 °C
@Time 14400 sec
176 °F
@Time 4.00 hour
 
Moisture Content  0.20 % 0.20 %
广泛用于制造机械、汽车、化学与电气装置的零件,如齿轮、滚子、滑轮、辊轴、泵体中叶轮、风扇叶片、高压密封围、阀座、垫片、衬套、各种把手、支撑架、电线包层等。亦可制成薄膜用作包装材料。此外,还可用于制作医疗器械、体育用品、日用品等。
 
上海松翰塑化科技有限公司,供应原料,品质真实,物实价廉。
PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。
欢迎各位客户前来咨询:
联系人: 夏先生  
手  机:13501802636   
QQ    :205730283  
邮 箱 :205730283@qq.com 
 

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/news/

本文链接: http://www.su-jiao.com/news/show-27001.html

免责声明: 本文 PA6 BFR460A 阻燃,注塑成型、 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4