颗粒：
、
、物性表:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.013 cm/cm @Thickness 4.00 mm |
0.013 in/in @Thickness 0.157 in |
E2P method |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 57.0 MPa | 8270 psi | 5 mm/min; ISO 527 |
| Tensile Strength, Yield | 69.0 MPa | 10000 psi | 5 mm/min; ISO 527 |
| Elongation at Yield | 3.5 % | 3.5 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 3.20 GPa | 464 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 97.0 MPa | 14100 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.50 GPa | 363 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80x10x4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 115 kJ/m² | 54.7 ft-lb/in² | 80x10x4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 164 °C | 327 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 58.0 °C | 136 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Af |
| Flammability, UL94 | V-2 @Thickness 0.800 mm |
V-2 @Thickness 0.0315 in |
|
| Processing Properties | Metric | English | Comments |
| Zone 1 | 240 - 250 °C | 464 - 482 °F | |
| Zone 2 | 250 - 260 °C | 482 - 500 °F | |
| Zone 3 | 250 - 270 °C | 482 - 518 °F | |
| Melt Temperature | 250 - 270 °C | 482 - 518 °F | |
| Mold Temperature | 50.0 - 90.0 °C | 122 - 194 °F | |
| Drying Temperature | 80.0 °C @Time 14400 sec |
176 °F @Time 4.00 hour |
|
| Moisture Content | 0.20 % | 0.20 % | |
广泛用于制造机械、汽车、化学与电气装置的零件，如齿轮、滚子、滑轮、辊轴、泵体中叶轮、风扇叶片、高压密封围、阀座、垫片、衬套、各种把手、支撑架、电线包层等。亦可制成薄膜用作包装材料。此外，还可用于制作医疗器械、体育用品、日用品等。