| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.06 g/cc | 0.0383 lb/in³ | ISO 1183 | ||
| Water Absorption | 9.0 % | 9.0 % | ISO 62 | ||
| Moisture Absorption | 3.00 % | 3.00 % | ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.011 cm/cm | 0.011 in/in | ISO 294-4, 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.014 cm/cm | 0.014 in/in | ISO 294-4, 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 40.0 MPa | 5800 psi | conditioned; ISO 2039-1 | ||
| 95.0 MPa | 13800 psi | dry; ISO 2039-1 | |||
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | dry; ISO 527-1/-2 | ||
| 50.0 MPa | 7250 psi | dry; ISO 527-1/-2 | |||
| Elongation at Break | >= 50 % | >= 50 % | conditioned; ISO 527-1/-2 | ||
| <= 50 % | <= 50 % | dry; ISO 527-1/-2 | |||
| Elongation at Yield | 4.0 % | 4.0 % | dry; ISO 527-1/-2 | ||
| 15 % | 15 % | conditioned; ISO 527-1/-2 | |||
| Tensile Modulus | 0.600 GPa | 87.0 ksi | conditioned; ISO 527-1/-2 | ||
| 1.80 GPa | 261 ksi | dry; ISO 527-1/-2 | |||
| Charpy Impact Unnotched | NB | NB | dry; ISO 179/1eU | ||
| NB | NB | conditioned; ISO 179/1eU | |||
| NB @Temperature 30.0 °C |
NB @Temperature 86.0 °F |
dry; ISO 179/1eU | |||
| NB @Temperature 30.0 °C |
NB @Temperature 86.0 °F |
conditioned; ISO 179/1eU | |||
| Charpy Impact, Notched | 6.50 J/cm² | 30.9 ft-lb/in² | dry; ISO 179/1eA | ||
| 11.5 J/cm² | 54.7 ft-lb/in² | conditioned; ISO 179/1eA | |||
| 1.50 J/cm² @Temperature 30.0 °C |
7.14 ft-lb/in² @Temperature 86.0 °F |
dry; ISO 179/1eU | |||
| 1.50 J/cm² @Temperature 30.0 °C |
7.14 ft-lb/in² @Temperature 86.0 °F |
conditioned; ISO 179/1eU | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | conditioned; IEC 60093 | ||
| 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | dry; IEC 60093 | |||
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 | ||
| Dielectric Strength | 39.0 kV/mm | 991 kV/in | conditioned; IEC 60243-1 | ||
| 42.0 kV/mm | 1070 kV/in | dry; IEC 60243-1 | |||
| Comparative Tracking Index | 600 V | 600 V | conditioned; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 130 µm/m-°C | 72.2 µin/in-°F | ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 150 µm/m-°C | 83.3 µin/in-°F | ISO 11359-1/-2 | ||
| Melting Point | 222 °C | 432 °F | 10°C/min; ISO 11357-1/-3 | ||
| Maximum Service Temperature, Air | 80.0 - 110 °C | 176 - 230 °F | long term; EMS | ||
| 160 °C | 320 °F | short term; EMS | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 130 °C | 266 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | ISO 75-1/-2 | ||
| Flammability, UL94 | HB | HB | IEC 60695-11-10 | ||
| De |
|||||
| Electricals & Electronics | Cables & Tubes | ||||
| Food contact | EU Requirements | ||||
| FDA | |||||
| Form | Granules | ||||
| Industry & Consumer goods | Hydraulics & Pneumatics | ||||
| Mechanical Engineering | |||||
| Power transmission | |||||
| Tools & Accessories | |||||
| Packaging | Blow moulded containers | ||||
| Injectionstretchblowmoulded containers | |||||
| Processing | Extrusion - blow molding | ||||
| Injection Molding | |||||
| Other Extrusion | |||||
| Product Attributes | Barrier Properties | ||||
| Flexible | |||||
| Special Characteristics | High impact or impact modified | ||||
广泛用于制造机械、汽车、化学与电气装置的零件，如齿轮、滚子、滑轮、辊轴、泵体中叶轮、风扇叶片、高压密封围、阀座、垫片、衬套、各种把手、支撑架、电线包层等。亦可制成薄膜用作包装材料。此外，还可用于制作医疗器械、体育用品、日用品等。