PA6 BRZ 347W PA6 耐冲击强度、_产品资讯

PA6 BRZ 347W 性状为半透明或不透明乳白色结晶形聚合物，具有可塑性。密度1．15g／cm3。熔点252℃。脆化温度-30℃。热分解温度大于350℃。连续耐热80-120℃,平衡吸水率2．5％。能耐酸、碱、大多数无机盐水溶液、卤代烷、烃类、酯类、酮类等腐蚀，但易溶于苯酚、甲酸等极性溶剂。具有优良的耐磨性、自润滑性，机械强度较高。但吸水性较大，因而尺寸稳定性较差。

颗粒：

、

物性表:

Physical Properties	Metric	English	Comments

Density	1.07 g/cc	0.0387 lb/in³	ISO 1183
Water Absorption	8.0 %	8.0 %	ISO 62
Moisture Absorption	2.50 %	2.50 %	ISO 62

Mechanical Properties	Metric	English	Comments
Ball Indentation Hardness	25.0 MPa	3630 psi	conditioned; ISO 2039-1
	35.0 MPa	5080 psi	dry; ISO 2039-1
Tensile Stress	25.0 MPa @Strain 50.0 %	3630 psi @Strain 50.0 %	conditioned; ISO 527-1/-2
	30.0 MPa @Strain 50.0 %	4350 psi @Strain 50.0 %	dry; ISO 527-1/-2
Elongation at Break	>= 50 %	>= 50 %	dry; ISO 527-1/-2
	>= 50 %	>= 50 %	conditioned; ISO 527-1/-2
Tensile Modulus	0.350 GPa	50.8 ksi	conditioned; ISO 527-1/-2
	0.600 GPa	87.0 ksi	dry; ISO 527-1/-2
Charpy Impact Unnotched	NB	NB	dry; ISO 179/1eU
	NB	NB	conditioned; ISO 179/1eU
	NB @Temperature 30.0 °C	NB @Temperature 86.0 °F	dry; ISO 179/1eU
	NB @Temperature 30.0 °C	NB @Temperature 86.0 °F	conditioned; ISO 179/1eU
Charpy Impact, Notched	11.0 J/cm²	52.3 ft-lb/in²	dry; ISO 179/1eA
	NB	NB	conditioned; ISO 179/1eA
	1.50 J/cm² @Temperature 30.0 °C	7.14 ft-lb/in² @Temperature 86.0 °F	dry; ISO 179/1eU
	1.50 J/cm² @Temperature 30.0 °C	7.14 ft-lb/in² @Temperature 86.0 °F	conditioned; ISO 179/1eU

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+13 ohm-cm	1.00e+13 ohm-cm	conditioned; IEC 60093
	1.00e+14 ohm-cm	1.00e+14 ohm-cm	dry; IEC 60093
Surface Resistance	1.00e+12 ohm	1.00e+12 ohm	IEC 60093
Comparative Tracking Index	600 V	600 V	conditioned; IEC 60112

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	150 µm/m-°C	83.3 µin/in-°F	ISO 11359-1/-2
CTE, linear, Transverse to Flow	160 µm/m-°C	88.9 µin/in-°F	ISO 11359-1/-2
Melting Point	215 °C	419 °F	10°C/min; ISO 11357-1/-3
Maximum Service Temperature, Air	80.0 - 110 °C	176 - 230 °F	long term; EMS
	150 °C	302 °F	short term; EMS
Deflection Temperature at 0.46 MPa (66 psi)	80.0 °C	176 °F	ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)	40.0 °C	104 °F	ISO 75-1/-2
Flammability, UL94	HB	HB	IEC 60695-11-10

Descriptive Properties
Additives	Plasticizer
Automotive	Air intake sytems
	Cooling and climate control
Electricals & Electronics	Cables & Tubes
Form	Granules
Industry & Consumer goods	Hydraulics & Pneumatics
	Mechanical Engineering
	Power transmission
Processing	Other Extrusion
Product Attributes	Flexible
Special Characteristics	High impact or impact modified

广泛用于制造机械、汽车、化学与电气装置的零件，如齿轮、滚子、滑轮、辊轴、泵体中叶轮、风扇叶片、高压密封围、阀座、垫片、衬套、各种把手、支撑架、电线包层等。亦可制成薄膜用作包装材料。此外，还可用于制作医疗器械、体育用品、日用品等。