TPU MVT 80AF3 物性表：
个别产品成品图片
TPU MVT 80AF3 物性表：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.21 g/cc | 1.21 g/cc | ASTM D792 |
| Water Vapor Transmission | 650 g/m²/day @Temperature 23.0 °C |
41.9 g/100 in²/day @Temperature 73.4 °F |
50% RH, Upright Cup, Water; ASTM E96B |
| 6000 g/m²/day @Temperature 38.0 °C |
386 g/100 in²/day @Temperature 100 °F |
98% RH, Upright Cup, Water; MOCON | |
| 9500 g/m²/day @Temperature 38.0 °C |
612 g/100 in²/day @Temperature 100 °F |
90% RH, Upright Cup, Desiccant; ASTM E96E | |
| Melt Flow | 54 g/10 min @Load 8.70 kg, Temperature 190 °C |
54 g/10 min @Load 19.2 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 80 | 80 | ASTM D2240 |
| Hardness, Shore D | 77 - 83 | 77 - 83 | ASTM D2240 |
| Tensile Strength, Ultimate | 27.6 MPa | 4000 psi | ASTM D412/D638 |
| Elongation at Break | 800 % | 800 % | Ultimate; ASTM D412/D638 |
| Tensile Modulus | 0.0138 GPa | 2.00 ksi | 500%; ASTM D412/D638 |
| 100% Modulus | 0.00410 GPa | 0.595 ksi | ASTM D412/D638 |
| 300% Modulus | 0.00690 GPa | 1.00 ksi | ASTM D412/D638 |
| Tear Strength | 16.7 kN/m | 95.0 pli | Split Tear Resistance; ASTM D470 |
| 68.4 kN/m | 390 pli | Die C; ASTM D624 | |
| Taber Abrasion, mg/1000 Cycles | 81 @Load 1.00 kg |
81 @Load 2.20 lb |
H-18 wheel; ASTM D3389 B |
| Compression Set | 17 % @Load 0.0000224 kg, Temperature 23.0 °C |
17 % @Load 0.0000484 lb, Temperature 73.4 °F |
ASTM D395 |
| Tensile Set | 10 % | 10 % | 200% elongation; ASTM D412 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 68.0 °C | 154 °F | ASTM D1525 |
| Processing Properties | Metric | English | Comments |
| Zone 1 | 166 - 177 °C | 331 - 351 °F | Extrusion |
| Zone 2 | 170 - 182 °C | 338 - 360 °F | Extrusion |
| Zone 3 | 177 - 188 °C | 351 - 370 °F | Extrusion |
| Zone 4 | 182 - 193 °C | 360 - 379 °F | Extrusion |
| Adapter Temperature | 182 - 193 °C | 360 - 379 °F | Extrusion |
| Die Temperature | 177 - 188 °C | 351 - 370 °F | Zone 2, Extrusion |
| 182 - 193 °C | 360 - 379 °F | Zone 1, Extrusion | |
| Screw Speed | 15 - 40 rpm | 15 - 40 rpm |
|
应用介绍：
1．薄膜和片材（TPU具较好耐磨性、抗刺穿性、抗撕裂性、弹性、粘合性）（TPU薄膜应用在冬季服装、鞋类具有防寒、保暖、防水性能好等特性外还具有特别好的透气性）
2．管材（TPU具有高伸长率，良好耐水解和抗微生物性、耐油性、优异机械性能，如作消防水管内衬，输油管气动软管等）
3．鞋底，鞋邦等鞋材料（TPU具有突出耐磨性、抗刮性、耐刺穿性、抗纵向弯曲强度和低温冲击强度，其耐撕裂性和抗裂纹传播性是所有塑料中最好的。如作溜冰、滑雪靴、运动鞋、特种功能鞋等）
4．电线、电缆、光缆护套（TPU具良好耐磨性、耐环境、耐候性、耐腐蚀性、绝缘性、弹性和低温柔韧性等）
5．拉链片、高档塑料表带、表壳以及潜水表、礼品表等系列（TPU具有高弹、耐折、耐水性好手感舒适等）
6．机械制品和其它应用（如制造汽车部件、机械轴承、滚轮、输送带、橡塑筛网、工业胶管,垫圈,密封圈,游泳镜,冲浪板,表带,动物标牌,电器零部件,涂料,粘合剂,纤维等.)
上海松翰塑化科技有限公司供应产品，品质一流，TPV种类齐全。 公司理念你的要求就是我们的追求 。咨询人夏先生 电话：13751253137 QQ：205730283 我公司将给你最专业产品加工工艺指导及帮你解决加工工艺难题 欢迎你的咨询